NDLI: Cu Bumping Characterization of Bond Pad and Underlying Structures and its Impact to Cratering

Content Provider	IEEE Xplore Digital Library
Author	Livelo, E. Ansay, I.C.
Copyright Year	2008
Description	Author affiliation: Fairchild Semicond., Portland, ME (Livelo, E.; Ansay, I.C.)
Abstract	Copper wirebonding process has gained semiconductor industry's attention for power and discrete devices due to its cost reduction and device electrical advantages over the conventional gold bonding process. Copper wire has several advantages over gold which includes the following properties: (1) Cu is lower in material cost than Au by 30-70% (2) Cu wire has higher conductivity property which allows higher current carrying capacity than Au. (3) Cu wire has stronger mechanical properties allowing a stronger heat affected zone, stable looping and sag wire control. (4) Cu-Al has slower intermetallic growth than Au-Al, allowing better mechanical stability and higher reliability. Compared to Au-Al bonding, there is a need to understand the amount of IMC in Cu ball bonds. A well known feature of the Cu bonds is that Ball shears away from the metallization leaving deformed Al and no traces of Cu. The "lack of Cu remains" is a known behavior of the Cu wire compared to Au, but does not mean that the ball bond is inferior. Even there is high ball shear strength of Cu wirebonding, interaction thickness of IMC can be hardly found because of its small dimension. Since Cu-Al phases grow very slowly compared to Au-Al, the rate of intermetallic growth between Cu-Al interphase is 2 to 2.5 times slower than that of the Au/Al interphase at constant temperature. It is difficult to observe interphase growth in a reasonable timeframe at normal HTS temperature like 150degC and 175degC. The Cu/Al IMC needs high thermal activation energy for propagation, which makes Cu a reliable material for bonding. Over its known advantages to gold, copper wire has material characteristics which need careful process and equipment characterization. The two major Cu characteristics over Au are: (1) Cu wire oxidizes readily compared to Au (2) Cu is relatively harder than Au. Since Copper wire oxidizes easily during sparking, there is a relative difficulty to maintain a consistent Free Air Ball (FAB) for Cu than Au due to oxidation. Equipment and parametric modifications are needed to prepare the machine for Cu bonding. Since Cu uses higher ultrasonic and bonding parameters than Au, assessing the spark generator capability is necessary. Oxidized Free Air Ball makes bonding susceptible to bonding failures and prone to crater since oxidization makes the Free Air ball harder. The use of forming gas, higher $H_{2}$ ratio and flow rate controls to prevent free air ball oxidation must be comprehended. Modification of the forming gas nozzle is also necessary to properly supply enough flow of forming gas during sparking. Since Cu FAB oxidizes very easily, equipment parametric adjustment needs to be characterized to allow a minimal exposure time of the Free Air Ball prior to bonding to prevent hardening of the ball. Compared to Au bonding process where the FAB is initially formed prior to the descent of the bondhead to bonding area, in Cu bonding process, free Air Ball formation is done simultaneously during the downward descent of the bondhead to the bonding pad. This allows shorter exposure of the Cu Free Air ball to bonding. Cratering has high susceptibility to occur in Copper bonding than Gold bonding due to the relative hardness of the Cu wire. The process requires higher bonding parameters associated with bonding Copper. To prevent cratering and bond pad damage, the need to thoroughly understand the bond pad material structure and underlying property is critical to check the impact of the bonding process to the bond pad material. In this study, experiments were done to determine the optimum bond pad property for Cu bonding. The amount of aluminum remaining under the Cu ball can be an indication of the level of stress associated with bonding Cu. Experiments using varying levels of Aluminum thickness, barrier metal thickness and structures were evaluated. The study recommends maintaining a consistent form of barrier metal structure to withstand cratering.
Starting Page	1321
Ending Page	1327
File Size	7654567
Page Count	7
File Format	PDF
ISBN	9781424421176
DOI	10.1109/EPTC.2008.4763614
Language	English
Publisher	Institute of Electrical and Electronics Engineers, Inc. (IEEE)
Publisher Date	2008-12-09
Publisher Place	Singapore
Access Restriction	Subscribed
Rights Holder	Institute of Electrical and Electronics Engineers, Inc. (IEEE)
Subject Keyword	Copper Gold Wire Bonding processes Mechanical factors Costs Intermetallic Materials reliability Temperature Oxidation
Content Type	Text
Resource Type	Article

Sl.	Authority	Responsibilities	Communication Details
1	Ministry of Education (GoI), Department of Higher Education	Sanctioning Authority	https://www.education.gov.in/ict-initiatives
2	Indian Institute of Technology Kharagpur	Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project	https://www.iitkgp.ac.in
3	National Digital Library of India Office, Indian Institute of Technology Kharagpur	The administrative and infrastructural headquarters of the project	Dr. B. Sutradhar bsutra@ndl.gov.in
4	Project PI / Joint PI	Principal Investigator and Joint Principal Investigators of the project	Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon
5	Website/Portal (Helpdesk)	Queries regarding NDLI and its services	support@ndl.gov.in
6	Contents and Copyright Issues	Queries related to content curation and copyright issues	content@ndl.gov.in
7	National Digital Library of India Club (NDLI Club)	Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach	clubsupport@ndl.gov.in
8	Digital Preservation Centre (DPC)	Assistance with digitizing and archiving copyright-free printed books	dpc@ndl.gov.in
9	IDR Setup or Support	Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops	idr@ndl.gov.in

Reliability study of low cost alternative Ag bonding wire with various bond pad materials

Surface-enhanced copper bonding wire for LSI and its bond reliability under humid environment

Reliability Results of 0.8 mil Fine Pitch Copper wire bonding on Immersion Gold Plated Pad for Copper Low-k Devices

Study on bond pad damage issue in bare Cu wire bonding on SMOS8MV wafer technology

Fine pitch copper wire bonding — Why now?

Copper wire reliability and bonding integrity robustness on cratering sensitive bond pad structure

High temperature performance study of gold wire bonding on a palladium bonding pad

Cu wire bond reliability improvement through focused heat treatment after bonding

Effects of Cu/Al intermetallic compound (IMC) on copper wire and aluminum pad bondability

Cu Bumping Characterization of Bond Pad and Underlying Structures and its Impact to Cratering

Similar Documents

Reliability study of low cost alternative Ag bonding wire with various bond pad materials

Surface-enhanced copper bonding wire for LSI and its bond reliability under humid environment

Reliability Results of 0.8 mil Fine Pitch Copper wire bonding on Immersion Gold Plated Pad for Copper Low-k Devices

Study on bond pad damage issue in bare Cu wire bonding on SMOS8MV wafer technology

Fine pitch copper wire bonding — Why now?

Copper wire reliability and bonding integrity robustness on cratering sensitive bond pad structure

High temperature performance study of gold wire bonding on a palladium bonding pad

Cu wire bond reliability improvement through focused heat treatment after bonding

Effects of Cu/Al intermetallic compound (IMC) on copper wire and aluminum pad bondability

Cu Bumping Characterization of Bond Pad and Underlying Structures and its Impact to Cratering