NDLI: Enhanced apatite formation on Ti metal heated in PO2-controlled nitrogen atmosphere.

Content Provider	World Health Organization (WHO)-Global Index Medicus
Author	Hashimoto, Masami Hayashi, Kazumi Kitaoka, Satoshi
Description	Author Affiliation: Hashimoto M ( Japan Fine Ceramics Center, 2-4-1 Mutsuno, Nagoya, 456-8587 Japan. masami@jfcc.or.jp)
Abstract	The oxynitridation of biomedical titanium metal under a precisely regulated oxygen partial pressure (PO2) of 10(-14)Pa in nitrogen atmosphere at 973 K for 1 h strongly enhanced apatite formation compared with that on Ti heated in air. The factors governing the high apatite-forming ability are discussed from the viewpoint of the surface properties of Ti heated under a PO2 of 10(-14)Pa in nitrogen atmosphere determined from X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and zeta potential measurements. Nitrogen (N)-doped TiO2 (interstitial N) was formed on pure Ti heated under a PO2 of 10(-14)Pa in nitrogen atmosphere at 973 K. The XPS O1s main peak shifted toward a lower binding energy upon heating under a PO2 of 10(-14)Pa. This shift may be due to the formation of oxygen vacancies. This Ti surface had a positive zeta potential of approximately 20 mV. According to time-of-flight secondary ion mass spectroscopy results, PO4(3-) ions were predominantly adsorbed on Ti soaked in simulated body fluid (SBF) after heat treatment, followed by calcium ions. It was concluded that the apatite formation kinetics can be described using the Avrami-Erofeev equation with an Avrami index of n=2, which implies the instantaneous nucleation of apatite on the surface of Ti soaked in SBF after heat treatment at 973 K under a PO2 of 10(-14)Pa.
File Format	HTM / HTML
ISSN	09284931
Issue Number	7
Volume Number	33
e-ISSN	18730191
Journal	Materials Science and Engineering: C
Language	English
Publisher	Elsevier
Publisher Date	2013-10-01
Publisher Place	Netherlands
Access Restriction	Subscribed
Subject Keyword	Discipline Materials Science Apatites Chemical Synthesis Hot Temperature Nitrogen Chemistry Oxygen Titanium Microscopy, Electron, Scanning Partial Pressure Photoelectron Spectroscopy Static Electricity X-ray Diffraction Journal Article Research Support, Non-u.s. Gov't
Content Type	Text
Resource Type	Article
Subject	Mechanics of Materials Biomaterials Condensed Matter Physics Bioengineering Mechanical Engineering

Sl.	Authority	Responsibilities	Communication Details
1	Ministry of Education (GoI), Department of Higher Education	Sanctioning Authority	https://www.education.gov.in/ict-initiatives
2	Indian Institute of Technology Kharagpur	Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project	https://www.iitkgp.ac.in
3	National Digital Library of India Office, Indian Institute of Technology Kharagpur	The administrative and infrastructural headquarters of the project	Dr. B. Sutradhar bsutra@ndl.gov.in
4	Project PI / Joint PI	Principal Investigator and Joint Principal Investigators of the project	Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon
5	Website/Portal (Helpdesk)	Queries regarding NDLI and its services	support@ndl.gov.in
6	Contents and Copyright Issues	Queries related to content curation and copyright issues	content@ndl.gov.in
7	National Digital Library of India Club (NDLI Club)	Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach	clubsupport@ndl.gov.in
8	Digital Preservation Centre (DPC)	Assistance with digitizing and archiving copyright-free printed books	dpc@ndl.gov.in
9	IDR Setup or Support	Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops	idr@ndl.gov.in