NDLI: Computational parametric study on the strain hardening effect of lead-free solder joints in board level mechanical drop tests

Content Provider	IEEE Xplore Digital Library
Author	Tong Jiang Xu Zhengjian Lee, S.W.R. Fubin Song Lo, J.C.C. Chaoran Yang
Copyright Year	2011
Description	Author affiliation: Electronic Packaging Laboratory, Center for Advanced Microsystems Packaging, Hong Kong University of Science and Technology, Clear Water Bay, Kowloon, Hong Kong (Tong Jiang; Xu Zhengjian; Lee, S.W.R.; Fubin Song; Lo, J.C.C.; Chaoran Yang)
Abstract	Many lead-free solder alloys have been proposed as alternatives to the conventional eutectic Sn-37wt%Pb (SnPb). This replacement induces the drop/impact reliability issues of portable products. Under the drop/impact loading, the main failure mode is interfacial brittle failure between lead-free solder joints and intermetallic compound (IMC) layer. The identification of failure mechanism in the solder joint under drop test becomes a very critical issue. In this paper, a finite element analysis of BGA assembly with lead-free solder joints is conducted to investigate IMC interfacial stresses under repetitive mechanical drops. For the two drop conditions of concern, the dominant strain rates for the solder joints are studied. The results indicate that the stress on the PCB side is larger than that on the package side in both the solder and the IMC. After multiple drops, the stress in the IMC gradually increases due to the strain hardening effect of the solder. During the repetitive drop tests, the increasing stress will eventually exceed the strength of IMC and leads to the brittle fracture of solder joint. The findings in the present study result in a better understanding in the failure mechanism of solder joint under repetitive mechanical drop tests.
Starting Page	1
Ending Page	6
File Size	1471760
Page Count	6
File Format	PDF
ISBN	9781467306942
e-ISBN	9780956808608
Language	English
Publisher	Institute of Electrical and Electronics Engineers, Inc. (IEEE)
Publisher Date	2011-09-12
Publisher Place	United Kingdom
Access Restriction	Subscribed
Rights Holder	IMAPS
Subject Keyword	stress ISO Lead Electromagnetic compatibility Iron Soldering Substrates lead-free solder IMC drop test
Content Type	Text
Resource Type	Article

Sl.	Authority	Responsibilities	Communication Details
1	Ministry of Education (GoI), Department of Higher Education	Sanctioning Authority	https://www.education.gov.in/ict-initiatives
2	Indian Institute of Technology Kharagpur	Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project	https://www.iitkgp.ac.in
3	National Digital Library of India Office, Indian Institute of Technology Kharagpur	The administrative and infrastructural headquarters of the project	Dr. B. Sutradhar bsutra@ndl.gov.in
4	Project PI / Joint PI	Principal Investigator and Joint Principal Investigators of the project	Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon
5	Website/Portal (Helpdesk)	Queries regarding NDLI and its services	support@ndl.gov.in
6	Contents and Copyright Issues	Queries related to content curation and copyright issues	content@ndl.gov.in
7	National Digital Library of India Club (NDLI Club)	Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach	clubsupport@ndl.gov.in
8	Digital Preservation Centre (DPC)	Assistance with digitizing and archiving copyright-free printed books	dpc@ndl.gov.in
9	IDR Setup or Support	Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops	idr@ndl.gov.in

Modeling of board level solder joint reliability under mechanical drop test with the consideration of plastic strain hardening of lead-free solder

Low silver lead-free solder joint reliability of VFBGA packages under board level drop test at −45°C

Low silver lead-free solder joint reliability of VFBGA packages under board level drop test at −45°C

Drop performance research of silver content on the SnAgCu based lead-free solder of joint level

Damage progression in BGA solder joints during board-level drop test

Effect of Solder Composition and Substrate Surface Finish on Board Level Drop Test Reliability

Comparison of mechanical properties of lead-free microscale solder joints under tensile and shear loading

Lead/Lead Free solder joints comparative shear tests function of working temperature and soldering thermal profile

Comprehensive modeling of stress-strain behavior for lead-free solder joints under board-level drop impact loading conditions

Computational parametric study on the strain hardening effect of lead-free solder joints in board level mechanical drop tests

Similar Documents

Modeling of board level solder joint reliability under mechanical drop test with the consideration of plastic strain hardening of lead-free solder

Low silver lead-free solder joint reliability of VFBGA packages under board level drop test at −45°C

Low silver lead-free solder joint reliability of VFBGA packages under board level drop test at −45°C

Drop performance research of silver content on the SnAgCu based lead-free solder of joint level

Damage progression in BGA solder joints during board-level drop test

Effect of Solder Composition and Substrate Surface Finish on Board Level Drop Test Reliability

Comparison of mechanical properties of lead-free microscale solder joints under tensile and shear loading

Lead/Lead Free solder joints comparative shear tests function of working temperature and soldering thermal profile

Comprehensive modeling of stress-strain behavior for lead-free solder joints under board-level drop impact loading conditions

Computational parametric study on the strain hardening effect of lead-free solder joints in board level mechanical drop tests