NDLI: Large transverse Seebeck voltage in oxygen-reduced $YBa_{2}Cu_{3}O/sub$ 7/ and Y/sub $1-x/Pr_{x}Ba_{2}Cu

Content Provider	IEEE Xplore Digital Library
Author	Lankes, F. Pechen, E.V. Honke, T. Renk, K.F.
Copyright Year	1996
Description	Author affiliation: Inst. of Appl. Phys., Regensburg Univ., Germany (Lankes, F.)
Abstract	The off-diagonal Seebeck voltage of oxygen-reduced YBa/sub 2/Cu/sub 3/O/sub 7/ and Y/sub 1-x/Pr/sub x/Ba/sub 2/Cu/sub 3/O/sub 7-/spl delta// thin films epitaxially grown on strontium titanate crystals cut with a tilt angle of 20/spl deg/ between substrate surface and the cubic axis was measured. A temperature gradient perpendicular to the film surface was produced at room temperature by exposing the films to UV radiation pulses. The transverse Seebeck voltage, i.e. the voltage parallel to the film surface, which results from the temperature gradient perpendicular to it, was measured for varying oxygen content and Pr doping of the YBa/sub 2/Cu/sub 3/O/sub 7-/spl delta// thin films. The oxygen content of the YBa/sub 2/Cu/sub 3/O/sub 7-/spl delta// thin films was reduced from /spl delta//spl sime/0 to /spl delta//spl sime/0.5. It is shown that a reduction of the oxygen content causes a decrease of the off-diagonal Seebeck voltage. The same effect is observed for the Y/sub 1-x/Pr/sub x/Ba/sub 2/Cu/sub 3/O/sub 7-/spl delta//(x= 0.1, 0.2, 0.3) thin films, i.e. raising the partial substitution of Y by Pr results in a smaller Seebeck voltage. These results suggest that both, oxygen reduction and Pr doping, have the effect of making YBa/sub 2/Cu/sub 3/O/sub 7-/spl delta// less anisotropic with respect to the thermopower. On the other hand, results of resistivity measurements of YBa/sub 2/Cu/sub 3/O/sub 7-/spl delta// with different values of /spl delta/ suggest that the anisotropy increases when oxygen is removed. A microscopic model for an explanation of the different behaviours of the thermopower and the resistivity is still lacking. We also have measured the transverse Seebeck voltage of YBa/sub 2/Cu/sub 3/O/sub 7-/spl delta//(/spl delta//spl sime/0.06 and 0.19) from T/sub c/ to room temperature. From this we can conclude that S/sub e/ of YBa/sub 2/Cu/sub 3/O/sub 7-/spl delta// (/spl delta//spl sime/0.06 and 0.19) increases linearly with temperature, i.e. S/sub c/ shows metallic behaviour.
Starting Page	494
Ending Page	498
File Size	551835
Page Count	5
File Format	PDF
ISBN	0780332210
DOI	10.1109/ICT.1996.553534
Language	English
Publisher	Institute of Electrical and Electronics Engineers, Inc. (IEEE)
Publisher Date	1996-03-26
Publisher Place	USA
Access Restriction	Subscribed
Rights Holder	Institute of Electrical and Electronics Engineers, Inc. (IEEE)
Subject Keyword	Voltage Transistors Doping Anisotropic magnetoresistance Strontium Titanium compounds Crystals Substrates Temperature measurement Conductivity measurement
Content Type	Text
Resource Type	Article

Sl.	Authority	Responsibilities	Communication Details
1	Ministry of Education (GoI), Department of Higher Education	Sanctioning Authority	https://www.education.gov.in/ict-initiatives
2	Indian Institute of Technology Kharagpur	Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project	https://www.iitkgp.ac.in
3	National Digital Library of India Office, Indian Institute of Technology Kharagpur	The administrative and infrastructural headquarters of the project	Dr. B. Sutradhar bsutra@ndl.gov.in
4	Project PI / Joint PI	Principal Investigator and Joint Principal Investigators of the project	Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon
5	Website/Portal (Helpdesk)	Queries regarding NDLI and its services	support@ndl.gov.in
6	Contents and Copyright Issues	Queries related to content curation and copyright issues	content@ndl.gov.in
7	National Digital Library of India Club (NDLI Club)	Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach	clubsupport@ndl.gov.in
8	Digital Preservation Centre (DPC)	Assistance with digitizing and archiving copyright-free printed books	dpc@ndl.gov.in
9	IDR Setup or Support	Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops	idr@ndl.gov.in

Reentrant Irreversibility and Magnetic Transition in Strongly Underdoped $Y{_0.47}Pr_{0.53}Ba_{2}Cu_{3}O_{7-\delta}$ Single Crystals

Homoepitaxial Growth of YBa_{2}Cu_{3}O_{7} on Single Crystal YBa_{2}Cu_{3}O_{x} Substrates

The effects of the misfit structure on thermoelectric properties of Bi/sub 2-x/Pb/sub x/Sr/sub 2/Co/sub 2/O/sub y/ single crystals

The CuO/sub 2/ interlayer coupling and anisotropic properties in Bi/sub 2/Sr/sub 2/Ca/sub 1-x/Gd/sub x/Cu/sub 2/O/sub 8+/spl delta// single crystals

Magnetoresistance in La/sub 0.7/Sr/sub 0.3/MnO/sub 3-/spl delta// biepitaxial grain boundary junction

Crystal growth of Pr(Ba/sub 4-x/Sr/sub 4/)/sub 2/Cu/sub 3/O/sub 7-y/

Quantum Creep in Y_{1-x}Pr_{x}Ba_{2}Cu_{3}O_{7}$ Crystals: Magnetic Relaxation and Transport

Fabrication and characterization of high quality NdBa/sub 2/Cu/sub 3/O/sub 7-/spl delta///Sr/sub 2/AlTaO/sub 6//NdBa/sub 2/Cu/sub 3/O/sub 7-/spl delta// and NdBa/sub 2/Cu/sub 3/O/sub 7-/spl delta///Sr/sub 2/AlNbO/sub 6//NdBa/sub 2/Cu/sub 3/O/sub 7-/spl delta// multilayers

Heat Diffusivity of Nd/sub 1-x/Sr/sub x/MnO/sub 3-/spl delta// and La/sub 1-x/Ca/sub x/MnO/sub 3-/spl delta//compounds

Large transverse Seebeck voltage in oxygen-reduced $YBa_{2}Cu_{3}O/sub$ 7/ and Y/sub $1-x/Pr_{x}Ba_{2}Cu_{3}O/sub$ 7-/spl delta// thin films

Similar Documents

Reentrant Irreversibility and Magnetic Transition in Strongly Underdoped $Y{_0.47}Pr_{0.53}Ba_{2}Cu_{3}O_{7-\delta}$ Single Crystals

Homoepitaxial Growth of YBa_{2}Cu_{3}O_{7} on Single Crystal YBa_{2}Cu_{3}O_{x} Substrates

The effects of the misfit structure on thermoelectric properties of Bi/sub 2-x/Pb/sub x/Sr/sub 2/Co/sub 2/O/sub y/ single crystals

The CuO/sub 2/ interlayer coupling and anisotropic properties in Bi/sub 2/Sr/sub 2/Ca/sub 1-x/Gd/sub x/Cu/sub 2/O/sub 8+/spl delta// single crystals

Magnetoresistance in La/sub 0.7/Sr/sub 0.3/MnO/sub 3-/spl delta// biepitaxial grain boundary junction

Crystal growth of Pr(Ba/sub 4-x/Sr/sub 4/)/sub 2/Cu/sub 3/O/sub 7-y/

Quantum Creep in Y_{1-x}Pr_{x}Ba_{2}Cu_{3}O_{7}$ Crystals: Magnetic Relaxation and Transport

Fabrication and characterization of high quality NdBa/sub 2/Cu/sub 3/O/sub 7-/spl delta///Sr/sub 2/AlTaO/sub 6//NdBa/sub 2/Cu/sub 3/O/sub 7-/spl delta// and NdBa/sub 2/Cu/sub 3/O/sub 7-/spl delta///Sr/sub 2/AlNbO/sub 6//NdBa/sub 2/Cu/sub 3/O/sub 7-/spl delta// multilayers

Heat Diffusivity of Nd/sub 1-x/Sr/sub x/MnO/sub 3-/spl delta// and La/sub 1-x/Ca/sub x/MnO/sub 3-/spl delta//compounds

Large transverse Seebeck voltage in oxygen-reduced $YBa_{2}Cu_{3}O/sub$ 7/ and Y/sub $1-x/Pr_{x}Ba_{2}Cu_{3}O/sub$ 7-/spl delta// thin films