| Abstract | Polydimethylsiloxane (PDMS) is the most popular and versatile material for soft lithography due to its flexibility and easy fabrication by molding process. However, for nanoscale patterns, it is challenging to fill uncured PDMS into the holes or trenches on the master mold that is coated with a silane anti-adhesion layer needed for clean demolding. PDMS filling was previously found to be facilitated by diluting it with toluene or hexane, which was attributed to the great reduction of viscosity for diluted PDMS. Here, we suggest that the reason behind the improved filling for diluted PDMS is that the diluent solvent increases in situ the surface energy of the silane-treated mold and thus the wetting of PDMS to the mold surface. We treated the master mold surface (that was already coated with a silane anti-adhesion monolayer) with toluene or hexane, and found that the filling by undiluted PMDS into the nanoscale holes on the master mold was improved despite the high viscosity of the undiluted PDMS. A simple estimation based on capillary filing into a channel also gives a filling time on the millisecond scale, which implies that the viscosity of PMDS should not be the limiting factor. We achieved a hole filling down to sub-200-nm diameter that is smaller than those of the previous studies using regular Sylgard PDMS (not hard PDMS, Dow Corning Corporation, Midland, MI, USA). However, we are not able to explain using a simple argument based on wetting property why smaller, e.g., sub-100-nm holes, cannot be filled, for which we suggested a few possible factors for its explanation. |
| Related Links | http://dx.doi.org/10.1186/1556-276x-8-394 |
| Starting Page | 394 |
| File Format | |
| ISSN | 1556276X |
| e-ISSN | 1556276X |
| Journal | Nanoscale Research Letters |
| Issue Number | 1 |
| Volume Number | 8 |
| Language | English |
| Publisher | Springer |
| Publisher Date | 2013-01-01 |
| Access Restriction | Open |
| Rights Holder | Springer |
| Subject Keyword | Materials Science(all) Condensed Matter Physics Research in Higher Education |
| Content Type | Text |
| Resource Type | Article |
| Subject | Nanoscience and Nanotechnology Condensed Matter Physics |
National Digital Library of India (NDLI) is a virtual repository of learning resources which is not just a repository with search/browse facilities but provides a host of services for the learner community. It is sponsored and mentored by Ministry of Education, Government of India, through its National Mission on Education through Information and Communication Technology (NMEICT). Filtered and federated searching is employed to facilitate focused searching so that learners can find the right resource with least effort and in minimum time. NDLI provides user group-specific services such as Examination Preparatory for School and College students and job aspirants. Services for Researchers and general learners are also provided. NDLI is designed to hold content of any language and provides interface support for 10 most widely used Indian languages. It is built to provide support for all academic levels including researchers and life-long learners, all disciplines, all popular forms of access devices and differently-abled learners. It is designed to enable people to learn and prepare from best practices from all over the world and to facilitate researchers to perform inter-linked exploration from multiple sources. It is developed, operated and maintained from Indian Institute of Technology Kharagpur.
Learn more about this project from here.
NDLI is a conglomeration of freely available or institutionally contributed or donated or publisher managed contents. Almost all these contents are hosted and accessed from respective sources. The responsibility for authenticity, relevance, completeness, accuracy, reliability and suitability of these contents rests with the respective organization and NDLI has no responsibility or liability for these. Every effort is made to keep the NDLI portal up and running smoothly unless there are some unavoidable technical issues.
Ministry of Education, through its National Mission on Education through Information and Communication Technology (NMEICT), has sponsored and funded the National Digital Library of India (NDLI) project.
| Sl. | Authority | Responsibilities | Communication Details |
|---|---|---|---|
| 1 | Ministry of Education (GoI), Department of Higher Education |
Sanctioning Authority | https://www.education.gov.in/ict-initiatives |
| 2 | Indian Institute of Technology Kharagpur | Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project | https://www.iitkgp.ac.in |
| 3 | National Digital Library of India Office, Indian Institute of Technology Kharagpur | The administrative and infrastructural headquarters of the project | Dr. B. Sutradhar bsutra@ndl.gov.in |
| 4 | Project PI / Joint PI | Principal Investigator and Joint Principal Investigators of the project |
Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon |
| 5 | Website/Portal (Helpdesk) | Queries regarding NDLI and its services | support@ndl.gov.in |
| 6 | Contents and Copyright Issues | Queries related to content curation and copyright issues | content@ndl.gov.in |
| 7 | National Digital Library of India Club (NDLI Club) | Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach | clubsupport@ndl.gov.in |
| 8 | Digital Preservation Centre (DPC) | Assistance with digitizing and archiving copyright-free printed books | dpc@ndl.gov.in |
| 9 | IDR Setup or Support | Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops | idr@ndl.gov.in |
|
Loading...
|