NDLI: Studies on the high-temperature superconductor (HTS)/metal/polymer dielectric interconnect structure for packaging applications

Content Provider	IEEE Xplore Digital Library
Author	Paik, K.W. Mogro-Campero, A.
Copyright Year	1994
Abstract	A HTS/metal/low dielectric constant polymer dielectric hybrid interconnect structure was fabricated using high density interconnect (HDI) copper/polyimide processing techniques. Nondegraded superconducting properties, J/sub c/ of over 1 MAcm/sup -2/ and T/sub c/ of 88 K, were obtained using optimum processing conditions. A 0.6 /spl mu/m-thick YBCO film was coevaporated on LaAlO/sub 3/ substrate, annealed, patterned, and Au contact pads were deposited. A Kapton polyimide film was laminated on HTS parts in an oxygen environment. Using a siloxane polyimide (SPI) base adhesive at 170-210/spl deg/C or a polyester base adhesive at 150/spl deg/C vias were drilled on the polymer layer using a 351 nm Ar laser followed by subsequent via cleaning with O/sub 2/+CF/sub 4/ plasma. To complete test parts Ti/Cu/Ti metallization and patterning with a laser adaptive lithography were followed. It was found that the laminated polymer film on the HTS protected HTS film properties from heating and water exposure. The polyimide laminated HTS film maintains its superconductivity up to 210/spl deg/C of lamination temperature. The hybrid structure also showed excellent reliability performances: 6% J/sub c/ decrease at 150/spl deg/C/65 h thermal bake, 12% J/sub c/ decrease after 100 thermal cycles from -96 to 150/spl deg/C, and maintain superconductivity in water immersion up to more than 10 h. T/sub c/ of samples remained always the same 88 K. Coplanar HTS lines, microstrip HTS/metal lines, and HTS power strip line structures were demonstrated on a 2-in-diameter HTS wafer coupon.<>
Sponsorship	IEEE Computer Society
Starting Page	435
Ending Page	441
Page Count	7
File Size	855709
File Format	PDF
ISSN	10709894
Volume Number	17
Issue Number	3
Language	English
Publisher	Institute of Electrical and Electronics Engineers, Inc. (IEEE)
Publisher Date	1994-08-01
Publisher Place	U.S.A.
Access Restriction	Subscribed
Rights Holder	Institute of Electrical and Electronics Engineers, Inc. (IEEE)
Subject Keyword	High temperature superconductors Polyimides Superconducting films Dielectric constant Polymer films Water heating Maintenance Superconductivity Yttrium barium copper oxide Substrates
Content Type	Text
Resource Type	Article
Subject	Engineering

Sl.	Authority	Responsibilities	Communication Details
1	Ministry of Education (GoI), Department of Higher Education	Sanctioning Authority	https://www.education.gov.in/ict-initiatives
2	Indian Institute of Technology Kharagpur	Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project	https://www.iitkgp.ac.in
3	National Digital Library of India Office, Indian Institute of Technology Kharagpur	The administrative and infrastructural headquarters of the project	Dr. B. Sutradhar bsutra@ndl.gov.in
4	Project PI / Joint PI	Principal Investigator and Joint Principal Investigators of the project	Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon
5	Website/Portal (Helpdesk)	Queries regarding NDLI and its services	support@ndl.gov.in
6	Contents and Copyright Issues	Queries related to content curation and copyright issues	content@ndl.gov.in
7	National Digital Library of India Club (NDLI Club)	Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach	clubsupport@ndl.gov.in
8	Digital Preservation Centre (DPC)	Assistance with digitizing and archiving copyright-free printed books	dpc@ndl.gov.in
9	IDR Setup or Support	Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops	idr@ndl.gov.in

Studies on the high temperature superconductor (HTS)/metal/polymer dielectric interconnect structure for packaging applications

High-temperature superconductor resonators and phase shifters

Microwave power handling capability of HTS superconducting thin films: weak links and thermal effects induced limitation

High-temperature superconducting oxide films

Submillimeter-wave properties of high-temperature superconductors and dielectrics using coherent time-domain spectroscopy

Nonlinear microwave properties of superconducting YBaCuO and dielectric MgO

Nonlinear Microwave Properties of Superconducting YBaCuO and Dielectric MgO

Large-area YBCO films for microwave applications

High-temperature superconductor-films microstrip band-pass filters for extreme working conditions

Studies on the high-temperature superconductor (HTS)/metal/polymer dielectric interconnect structure for packaging applications

Similar Documents

Studies on the high temperature superconductor (HTS)/metal/polymer dielectric interconnect structure for packaging applications

High-temperature superconductor resonators and phase shifters

Microwave power handling capability of HTS superconducting thin films: weak links and thermal effects induced limitation

High-temperature superconducting oxide films

Submillimeter-wave properties of high-temperature superconductors and dielectrics using coherent time-domain spectroscopy

Nonlinear microwave properties of superconducting YBaCuO and dielectric MgO

Nonlinear Microwave Properties of Superconducting YBaCuO and Dielectric MgO

Large-area YBCO films for microwave applications

High-temperature superconductor-films microstrip band-pass filters for extreme working conditions

Studies on the high-temperature superconductor (HTS)/metal/polymer dielectric interconnect structure for packaging applications