NDLI: Characteristic analysis of temperature-dependent photocurrent and photoluminescence spectra in as-implanted p-ZnO crystals

Content Provider	Springer Nature Link
Author	Youn, C. J. Hong, K. J. Kim, T. S. Yang, H. J. Yu, J. H. Mo, H. S. Jeong, T. S.
Copyright Year	2013
Abstract	The temperature-dependent photoresponse properties of As-doped p-ZnO crystals prepared by using the As-implantation method have been investigated by using photocurrent (PC) and photoluminescence (PL) spectroscopy. Two peaks, A and C, associated with band-to-band transitions were observed in the PC spectra. From the PL spectra, the neutral acceptor bound exciton emission, (A$^{0}$, X), due to As-related acceptors was extracted. The temperature dependences of these peaks were well described by E $_{ g }$(T) = E $_{ g }$(0) — (3.10 × 10$^{−4}$)T$^{2}$/(143 + T). Also, the values of E $_{ g }$(T) were estimated to be 3.412, 3.418, and 3.468 eV at the valence-band states of Γ$_{9}$(A), Γ$_{7}$(B), and Γ$_{7}$(C), respectively. Thus, the parameter of the crystal-field splitting was directly extracted by means of PC spectroscopy, and its value was 0.0503 eV at 13 K. However, the behavior of the PC was different from that generally observed in other semiconductors. The PC intensities progressively decreased with falling temperatures in regions below 150 K. From plots of log J $_{ PC }$ vs. 1/T, where J $_{ PC }$ is the PC current-density, a dominant level was observed at mid-range temperatures. By comparing the PC and the PL results, we confirmed an activation energy of 21.5 meV, corresponding to a partial dissociation energy of the (A$^{0}$, X) emission. Consequently, trapping centers, which are imperfections related to As ions in As-implanted p-ZnO crystals, are thought to limit the PC intensity with decreasing temperatures below 150 K.
Starting Page	1777
Ending Page	1783
Page Count	7
File Format	PDF
ISSN	03744884
Journal	Journal of the Korean Physical Society
Volume Number	63
Issue Number	9
e-ISSN	19768524
Language	English
Publisher	Springer Netherlands
Publisher Date	2013-11-23
Publisher Place	Dordrecht
Access Restriction	One Nation One Subscription (ONOS)
Subject Keyword	Temperature dependence Valence-band splitting p type Photocurrent Theoretical, Mathematical and Computational Physics Photoluminescence Implantation ZnO Physics Particle and Nuclear Physics
Content Type	Text
Resource Type	Article
Subject	Physics and Astronomy

Sl.	Authority	Responsibilities	Communication Details
1	Ministry of Education (GoI), Department of Higher Education	Sanctioning Authority	https://www.education.gov.in/ict-initiatives
2	Indian Institute of Technology Kharagpur	Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project	https://www.iitkgp.ac.in
3	National Digital Library of India Office, Indian Institute of Technology Kharagpur	The administrative and infrastructural headquarters of the project	Dr. B. Sutradhar bsutra@ndl.gov.in
4	Project PI / Joint PI	Principal Investigator and Joint Principal Investigators of the project	Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon
5	Website/Portal (Helpdesk)	Queries regarding NDLI and its services	support@ndl.gov.in
6	Contents and Copyright Issues	Queries related to content curation and copyright issues	content@ndl.gov.in
7	National Digital Library of India Club (NDLI Club)	Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach	clubsupport@ndl.gov.in
8	Digital Preservation Centre (DPC)	Assistance with digitizing and archiving copyright-free printed books	dpc@ndl.gov.in
9	IDR Setup or Support	Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops	idr@ndl.gov.in

Photoresponse-behavior analysis of ZnAl$_{2}$Se$_{4}$ layers by using photocurrent spectroscopy

Investigation of the temperature-dependent photoconductive behaviors of hot-wall-deposited MnAl$_{2}$Se$_{4}$ layers

Spectral behavior of the temperature-dependent photoresponse of BaAl$_{2}$S$_{4}$ layers grown by using hot-wall epitaxy

Temperature dependences of the intensity and the position from photocurrent and photoluminescence spectra in CdS layers

Behavior of temperature-dependent dc-photoconductivity in hot-wall deposited CaAl$_{2}$Se$_{4}$ layers

Temperature dependence of photocurrent spectra from MgGa$_{2}$Se$_{4}$ layers grown by using the hot-wall epitaxy method

Optical properties of ITO/ZnO Schottky diode with enhanced UV Photoresponse

Temperature dependence of the excitonic energy band gap in In(Ga)As nanostructures

Near-band-edge photoluminescence from ZnO film: Negative thermal quenching and role of adsorbed oxygen

Characteristic analysis of temperature-dependent photocurrent and photoluminescence spectra in as-implanted p-ZnO crystals

Similar Documents

Photoresponse-behavior analysis of ZnAl$_{2}$Se$_{4}$ layers by using photocurrent spectroscopy

Investigation of the temperature-dependent photoconductive behaviors of hot-wall-deposited MnAl$_{2}$Se$_{4}$ layers

Spectral behavior of the temperature-dependent photoresponse of BaAl$_{2}$S$_{4}$ layers grown by using hot-wall epitaxy

Temperature dependences of the intensity and the position from photocurrent and photoluminescence spectra in CdS layers

Behavior of temperature-dependent dc-photoconductivity in hot-wall deposited CaAl$_{2}$Se$_{4}$ layers

Temperature dependence of photocurrent spectra from MgGa$_{2}$Se$_{4}$ layers grown by using the hot-wall epitaxy method

Optical properties of ITO/ZnO Schottky diode with enhanced UV Photoresponse

Temperature dependence of the excitonic energy band gap in In(Ga)As nanostructures

Near-band-edge photoluminescence from ZnO film: Negative thermal quenching and role of adsorbed oxygen

Characteristic analysis of temperature-dependent photocurrent and photoluminescence spectra in as-implanted p-ZnO crystals