| Author | Park, Dong Wook Kim, Dae Hwan Kim, Hye Seong Kwon, Youg Sam Cho, Kwon Koo Lim, Su Gun Ahn, In Shup |
| Copyright Year | 2014 |
| Abstract | Tool steels have a large range of applications including hot and cold working of metals and injection molding of plastic or light alloys. High-speed steel (HSS) is specifically used for cutting tools and for components subjected to extreme wear conditions, because of its high strength, wear resistance, hardness, toughness, and fatigue resistance. The microstructure of HSS can be described as a metallic matrix iron composite containing a dispersion of hard and wear-resistant carbides. Specimens were manufactured experimentally from T42 powder (50–80 vol%) and mixed binder (20–50 vol%) by powder injection molding. The binders (green parts) were debound in n-hexane solution at 60 °C for 8 h and thermally debound in a mixed N$_{2}$–H$_{2}$ gas atmosphere for 8 h. Specimens were sintered under high vacuum (10$^{−5}$ Torr) at different temperatures. When sintering was performed at 1,260 °C, the specimen sintered under high vacuum had the highest hardness (550 Hv). The carbides were smaller (1 μm) and well distributed. Grain size was 10 μm. When sintering was performed under high vacuum at temperatures above 1,280 °C the carbides changed to eutectic carbide located at grain boundaries. Grain growth was observed. Specimens sintered at other pressures had lower density and hardness than those sintered under high vacuum. |
| Starting Page | 2415 |
| Ending Page | 2421 |
| Page Count | 7 |
| File Format | |
| ISSN | 09226168 |
| Journal | Research on Chemical Intermediates |
| Volume Number | 40 |
| Issue Number | 7 |
| e-ISSN | 15685675 |
| Language | English |
| Publisher | Springer Netherlands |
| Publisher Date | 2014-05-16 |
| Publisher Place | Dordrecht |
| Access Restriction | One Nation One Subscription (ONOS) |
| Subject Keyword | High-speed steel (HSS) Powder injection molding (PIM) Debinding Sintering Catalysis Physical Chemistry Inorganic Chemistry |
| Content Type | Text |
| Resource Type | Article |
| Subject | Chemistry |
National Digital Library of India (NDLI) is a virtual repository of learning resources which is not just a repository with search/browse facilities but provides a host of services for the learner community. It is sponsored and mentored by Ministry of Education, Government of India, through its National Mission on Education through Information and Communication Technology (NMEICT). Filtered and federated searching is employed to facilitate focused searching so that learners can find the right resource with least effort and in minimum time. NDLI provides user group-specific services such as Examination Preparatory for School and College students and job aspirants. Services for Researchers and general learners are also provided. NDLI is designed to hold content of any language and provides interface support for 10 most widely used Indian languages. It is built to provide support for all academic levels including researchers and life-long learners, all disciplines, all popular forms of access devices and differently-abled learners. It is designed to enable people to learn and prepare from best practices from all over the world and to facilitate researchers to perform inter-linked exploration from multiple sources. It is developed, operated and maintained from Indian Institute of Technology Kharagpur.
Learn more about this project from here.
NDLI is a conglomeration of freely available or institutionally contributed or donated or publisher managed contents. Almost all these contents are hosted and accessed from respective sources. The responsibility for authenticity, relevance, completeness, accuracy, reliability and suitability of these contents rests with the respective organization and NDLI has no responsibility or liability for these. Every effort is made to keep the NDLI portal up and running smoothly unless there are some unavoidable technical issues.
Ministry of Education, through its National Mission on Education through Information and Communication Technology (NMEICT), has sponsored and funded the National Digital Library of India (NDLI) project.
| Sl. | Authority | Responsibilities | Communication Details |
|---|---|---|---|
| 1 | Ministry of Education (GoI), Department of Higher Education |
Sanctioning Authority | https://www.education.gov.in/ict-initiatives |
| 2 | Indian Institute of Technology Kharagpur | Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project | https://www.iitkgp.ac.in |
| 3 | National Digital Library of India Office, Indian Institute of Technology Kharagpur | The administrative and infrastructural headquarters of the project | Dr. B. Sutradhar bsutra@ndl.gov.in |
| 4 | Project PI / Joint PI | Principal Investigator and Joint Principal Investigators of the project |
Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon |
| 5 | Website/Portal (Helpdesk) | Queries regarding NDLI and its services | support@ndl.gov.in |
| 6 | Contents and Copyright Issues | Queries related to content curation and copyright issues | content@ndl.gov.in |
| 7 | National Digital Library of India Club (NDLI Club) | Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach | clubsupport@ndl.gov.in |
| 8 | Digital Preservation Centre (DPC) | Assistance with digitizing and archiving copyright-free printed books | dpc@ndl.gov.in |
| 9 | IDR Setup or Support | Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops | idr@ndl.gov.in |
|
Loading...
|