| Author | Andersson, Henrik A. Thungström, Göran Nilsson, Hans Erik |
| Copyright Year | 2007 |
| Abstract | Porous Silicon (PS) has attracted much attention since the discovery of its photo luminescent behavior. It has also been used for various other applications such as electroluminescent light emitting-diodes (LEDs), photodetectors and solar cells. For such devices, it is important to make good metallic Ohmic contacts to the PS in order to maximize the efficiency. In order to produce buried contacts, barrier layers, Schottky devices, etc. in PS, it is advantageous to deposit metal that covers not only the surface of the porous layer, but also the inside walls and the bottom of the pores. In this work experiments were performed to examine the morphology and properties of electroless deposition of Nickel into p-type PS and subsequent formation of Nickel silicide after heat treatment. Circular PS samples of 6 mm diameter were produced by anodizing p-type Silicon wafers for 15 min and were subsequently plated with Ni using three different plating baths. The pores are on average 20 µm deep and 4 µm wide. Two samples of each type were heat treated in an nitrogen atmosphere for one hour at 400 and 600°C respectively to produce Nickel silicide. Reference samples were made by means of electron beam evaporation of Ni. SEM micrographs show that the best pore coverage was achieved using the Ni plating bath containing hypophosphite. I–V characterization shows that different rectifying and Ohmic contacts can be formed between electroless deposited Ni and PS depending on the conditions of the heat treatment. XRD and EDX characterizations show that both the NiSi and Ni$_{2}$Si phases exist in the sample at the same time. |
| Starting Page | 335 |
| Ending Page | 341 |
| Page Count | 7 |
| File Format | |
| ISSN | 13802224 |
| Journal | Journal of Porous Materials |
| Volume Number | 15 |
| Issue Number | 3 |
| e-ISSN | 15734854 |
| Language | English |
| Publisher | Springer US |
| Publisher Date | 2007-03-29 |
| Publisher Place | Boston |
| Access Restriction | One Nation One Subscription (ONOS) |
| Subject Keyword | Porous Silicon Electroless deposition Nickel Silicide Physical Chemistry Characterization and Evaluation of Materials Catalysis |
| Content Type | Text |
| Resource Type | Article |
| Subject | Mechanics of Materials Materials Science Mechanical Engineering |
National Digital Library of India (NDLI) is a virtual repository of learning resources which is not just a repository with search/browse facilities but provides a host of services for the learner community. It is sponsored and mentored by Ministry of Education, Government of India, through its National Mission on Education through Information and Communication Technology (NMEICT). Filtered and federated searching is employed to facilitate focused searching so that learners can find the right resource with least effort and in minimum time. NDLI provides user group-specific services such as Examination Preparatory for School and College students and job aspirants. Services for Researchers and general learners are also provided. NDLI is designed to hold content of any language and provides interface support for 10 most widely used Indian languages. It is built to provide support for all academic levels including researchers and life-long learners, all disciplines, all popular forms of access devices and differently-abled learners. It is designed to enable people to learn and prepare from best practices from all over the world and to facilitate researchers to perform inter-linked exploration from multiple sources. It is developed, operated and maintained from Indian Institute of Technology Kharagpur.
Learn more about this project from here.
NDLI is a conglomeration of freely available or institutionally contributed or donated or publisher managed contents. Almost all these contents are hosted and accessed from respective sources. The responsibility for authenticity, relevance, completeness, accuracy, reliability and suitability of these contents rests with the respective organization and NDLI has no responsibility or liability for these. Every effort is made to keep the NDLI portal up and running smoothly unless there are some unavoidable technical issues.
Ministry of Education, through its National Mission on Education through Information and Communication Technology (NMEICT), has sponsored and funded the National Digital Library of India (NDLI) project.
| Sl. | Authority | Responsibilities | Communication Details |
|---|---|---|---|
| 1 | Ministry of Education (GoI), Department of Higher Education |
Sanctioning Authority | https://www.education.gov.in/ict-initiatives |
| 2 | Indian Institute of Technology Kharagpur | Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project | https://www.iitkgp.ac.in |
| 3 | National Digital Library of India Office, Indian Institute of Technology Kharagpur | The administrative and infrastructural headquarters of the project | Dr. B. Sutradhar bsutra@ndl.gov.in |
| 4 | Project PI / Joint PI | Principal Investigator and Joint Principal Investigators of the project |
Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon |
| 5 | Website/Portal (Helpdesk) | Queries regarding NDLI and its services | support@ndl.gov.in |
| 6 | Contents and Copyright Issues | Queries related to content curation and copyright issues | content@ndl.gov.in |
| 7 | National Digital Library of India Club (NDLI Club) | Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach | clubsupport@ndl.gov.in |
| 8 | Digital Preservation Centre (DPC) | Assistance with digitizing and archiving copyright-free printed books | dpc@ndl.gov.in |
| 9 | IDR Setup or Support | Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops | idr@ndl.gov.in |
|
Loading...
|