| Author | Praveena, K. Sadhana, K. Liu, Hsiang Lin Murthy, S. R. |
| Copyright Year | 2016 |
| Abstract | Co$_{1−x}$Zn$_{x}$Fe$_{2}$O$_{4}$ (0 ≤ x ≥ 1) nanopowders were synthesized using microwave hydrothermal method. The synthesized powders were characterized by X-ray diffraction and transmission electron microscope (TEM). The average particle size was obtained from TEM and it is found to be 17 nm. Then powders were sintered using microwave sintering method at 900 °C/15 min. The real part of permittivity varies as Zn concentration increases and the resonance frequency was observed at much higher frequencies (>1 GHz) and there is a significant decrease in the loss factor. The dielectric parameters were observed to decrease with the increased Zn contents. The frequency dependent dielectric properties of all these nanomaterials have been explained qualitatively in accordance with Koop’s phenomenological theory. The magnetic permeability spectra exhibit resonance and anti-resonance type behaviour. Lower reduced remnant magnetization (M$_{r}$/M$_{s}$) values (x < 0.5) suggest that all the samples have uniaxial anisotropy. The increasing trend of magnetic parameters (coercivity and retentivity) is consistent with crystallinity. The moderate magnetization and high coercivity are enough to attain considerable signal to noise ratio in high density recording media. |
| Starting Page | 12680 |
| Ending Page | 12690 |
| Page Count | 11 |
| File Format | |
| ISSN | 09574522 |
| Journal | Journal of Materials Science: Materials in Electronics |
| Volume Number | 27 |
| Issue Number | 12 |
| e-ISSN | 1573482X |
| Language | English |
| Publisher | Springer US |
| Publisher Date | 2016-07-25 |
| Publisher Place | New York |
| Access Restriction | One Nation One Subscription (ONOS) |
| Subject Keyword | Optical and Electronic Materials Characterization and Evaluation of Materials |
| Content Type | Text |
| Resource Type | Article |
| Subject | Atomic and Molecular Physics, and Optics Biomaterials Biophysics Condensed Matter Physics Electronic, Optical and Magnetic Materials Bioengineering Electrical and Electronic Engineering Biomedical Engineering |
National Digital Library of India (NDLI) is a virtual repository of learning resources which is not just a repository with search/browse facilities but provides a host of services for the learner community. It is sponsored and mentored by Ministry of Education, Government of India, through its National Mission on Education through Information and Communication Technology (NMEICT). Filtered and federated searching is employed to facilitate focused searching so that learners can find the right resource with least effort and in minimum time. NDLI provides user group-specific services such as Examination Preparatory for School and College students and job aspirants. Services for Researchers and general learners are also provided. NDLI is designed to hold content of any language and provides interface support for 10 most widely used Indian languages. It is built to provide support for all academic levels including researchers and life-long learners, all disciplines, all popular forms of access devices and differently-abled learners. It is designed to enable people to learn and prepare from best practices from all over the world and to facilitate researchers to perform inter-linked exploration from multiple sources. It is developed, operated and maintained from Indian Institute of Technology Kharagpur.
Learn more about this project from here.
NDLI is a conglomeration of freely available or institutionally contributed or donated or publisher managed contents. Almost all these contents are hosted and accessed from respective sources. The responsibility for authenticity, relevance, completeness, accuracy, reliability and suitability of these contents rests with the respective organization and NDLI has no responsibility or liability for these. Every effort is made to keep the NDLI portal up and running smoothly unless there are some unavoidable technical issues.
Ministry of Education, through its National Mission on Education through Information and Communication Technology (NMEICT), has sponsored and funded the National Digital Library of India (NDLI) project.
| Sl. | Authority | Responsibilities | Communication Details |
|---|---|---|---|
| 1 | Ministry of Education (GoI), Department of Higher Education |
Sanctioning Authority | https://www.education.gov.in/ict-initiatives |
| 2 | Indian Institute of Technology Kharagpur | Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project | https://www.iitkgp.ac.in |
| 3 | National Digital Library of India Office, Indian Institute of Technology Kharagpur | The administrative and infrastructural headquarters of the project | Dr. B. Sutradhar bsutra@ndl.gov.in |
| 4 | Project PI / Joint PI | Principal Investigator and Joint Principal Investigators of the project |
Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon |
| 5 | Website/Portal (Helpdesk) | Queries regarding NDLI and its services | support@ndl.gov.in |
| 6 | Contents and Copyright Issues | Queries related to content curation and copyright issues | content@ndl.gov.in |
| 7 | National Digital Library of India Club (NDLI Club) | Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach | clubsupport@ndl.gov.in |
| 8 | Digital Preservation Centre (DPC) | Assistance with digitizing and archiving copyright-free printed books | dpc@ndl.gov.in |
| 9 | IDR Setup or Support | Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops | idr@ndl.gov.in |
|
Loading...
|