A microstructural observation of near-failure thermal barrier coating: a study by photostimulated luminescence spectroscopy and transmission electron microscopy

Content Provider	Semantic Scholar
Author	Kempshall, B. W. Sohn, Yeung H. Jha, Sandeep Kumar Laxman, S. Vanfleet, Richard R. Kimmel, Jyrki
Copyright Year	2004
Abstract	An intact thermal barrier coating (TBC) specimen, consisting of electron-beam physical vapor deposited (EB-PVD) ZrO2–7 wt.%Y2O3 (YSZ) topcoat, thermally grown oxide (TGO), grit-blasted (Ni,Pt)Al bond coat and CMSX-4 single crystalline superalloy, was characterized after 645 thermal cycles. Each thermal cycle was carried out in air, and consisted of 10-min heat-up to 1038 jC, 10-h hold at 1038 jC, and 10-min forced air-quench to ambient temperature. Characteristics of TGO scale were initially examined by photostimulated luminescence spectroscopy (PSLS) and scanning electron microscopy equipped with energy dispersive spectroscopy (EDS). Transmission electron microscopy (TEM) and scanning TEM (STEM) with nano-spot energy dispersive spectroscopy, high-angle annular dark field (HAADF) imaging, selected area diffraction (SAD), convergent beam electron diffraction (CBED), and electron energy loss spectroscopy was carried out for detailed microstructural characterization. A site-specific preparation of TEM specimen for the thermally cycled TBC was successfully carried out using focused ion beam in-situ lift out technique. Photostimulated luminescence corresponding to negligible residual stress in TGO scale was observed for this intact TBC. Microstructural analysis showed undulation of interface between TGO and bond coat, and the corresponding damage near YSZ/TGO interface. Extensive decohesion within TGO (nearly 9 Am thick), near the YSZ/TGO interface, was observed by TEM/STEM, and related to the observation made by PSLS. Microstructure and phase constituents of mixed-oxide zone containing Zr, Y, Ta, Ni, Co, Cr, Ti in Al2O3 matrix and continuous-columnar Al2O3 TGO are presented based on TEM/STEM and related analytical techniques. D 2004 Elsevier B.V. All rights reserved. PACS: 81.40.-z; 81.65.Mq
File Format	PDF HTM / HTML
Alternate Webpage(s)	http://www.nanospective.com/PDF/A_microstructural_observation_of_near_failure_thermal_barrier_coating.pdf
Language	English
Access Restriction	Open
Content Type	Text
Resource Type	Article

Central Library (ISO-9001:2015 Certified)
Indian Institute of Technology Kharagpur
Kharagpur, West Bengal, India | PIN - 721302

See location in the Map
03222 282435
Mail: support@ndl.gov.in

Sl.	Authority	Responsibilities	Communication Details
1	Ministry of Education (GoI), Department of Higher Education	Sanctioning Authority	https://www.education.gov.in/ict-initiatives
2	Indian Institute of Technology Kharagpur	Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project	https://www.iitkgp.ac.in
3	National Digital Library of India Office, Indian Institute of Technology Kharagpur	The administrative and infrastructural headquarters of the project	Dr. B. Sutradhar bsutra@ndl.gov.in
4	Project PI / Joint PI	Principal Investigator and Joint Principal Investigators of the project	Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon
5	Website/Portal (Helpdesk)	Queries regarding NDLI and its services	support@ndl.gov.in
6	Contents and Copyright Issues	Queries related to content curation and copyright issues	content@ndl.gov.in
7	National Digital Library of India Club (NDLI Club)	Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach	clubsupport@ndl.gov.in
8	Digital Preservation Centre (DPC)	Assistance with digitizing and archiving copyright-free printed books	dpc@ndl.gov.in
9	IDR Setup or Support	Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops	idr@ndl.gov.in