NDLI: Macroporous SmMn2O5 mullite for NOx-assisted soot combustion

Content Provider	Royal Society of Chemistry (RSC)
Author	Chen, Rong Liu, Qinhan Zhao, Pengfei Peng, Qi Shan, Bin Feng, Zijian Shen, Meiqing Chen, Yongjie Cao, Kun
Copyright Year	2017
Abstract	A series of mullite SmMn2O5 oxides were prepared by citric acid (CA), hydrothermal (HT) and co-precipitation (CP) and combustion of ethylene glycol and methanol solutions (EG&M) methods, and tested for NOx-assisted soot combustion. The catalyst performance tests were conducted under “loose” contact conditions and the physical and chemical properties characterized by XRD, FTIR, BET, SEM, XPS, and O2-TPD and H2-TPR measurements. The SmMn2O5-EG&M catalyst possessed a distinct morphology with slabs separated by interconnected macropores, and exhibited the overall highest catalytic activity for soot combustion. The corresponding T10, T50, and T90 were 283 °C, 368 °C, and 420 °C, respectively, and the CO2 selectivity was 99.6%. The soot combustion activation energy for the SmMn2O5-EG&M catalyst is 65 kJ mol−1. O2-TPD and H2-TPR measurements demonstrated higher mobility and better reducibility of surface adsorbed oxygen for the EG&M sample. The soot combustion is greatly accelerated by the NO2-assisted mechanism under a NO + O2 atmosphere and further enhanced by the interconnected macropores of the catalyst, facilitating an intimate contact between the soot and the catalyst. Our study reveals that SmMn2O5 mullite is an effective catalyst for NOx-assisted soot combustion.
Starting Page	838
Ending Page	847
Page Count	10
File Format	HTM / HTML PDF
ISSN	20444753
Volume Number	7
Issue Number	4
Journal	Catalysis Science & Technology
DOI	10.1039/c6cy02478e
Language	English
Publisher	Royal Society of Chemistry
Access Restriction	Open
Subject Keyword	BET X-ray crystallography Ethylene glycol Acid Oxygen Hydrothermal circulation Soot Mullite Intimate Contact Activation energy Coprecipitation Methanol
Content Type	Text
Resource Type	Article
Subject	Catalysis

Sl.	Authority	Responsibilities	Communication Details
1	Ministry of Education (GoI), Department of Higher Education	Sanctioning Authority	https://www.education.gov.in/ict-initiatives
2	Indian Institute of Technology Kharagpur	Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project	https://www.iitkgp.ac.in
3	National Digital Library of India Office, Indian Institute of Technology Kharagpur	The administrative and infrastructural headquarters of the project	Dr. B. Sutradhar bsutra@ndl.gov.in
4	Project PI / Joint PI	Principal Investigator and Joint Principal Investigators of the project	Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon
5	Website/Portal (Helpdesk)	Queries regarding NDLI and its services	support@ndl.gov.in
6	Contents and Copyright Issues	Queries related to content curation and copyright issues	content@ndl.gov.in
7	National Digital Library of India Club (NDLI Club)	Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach	clubsupport@ndl.gov.in
8	Digital Preservation Centre (DPC)	Assistance with digitizing and archiving copyright-free printed books	dpc@ndl.gov.in
9	IDR Setup or Support	Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops	idr@ndl.gov.in

Facile synthesis of catalytically active CeO₂ for soot combustion

Boosting soot combustion efficiencies over CuO–CeO₂ catalysts with a 3DOM structure

Three-dimensionally ordered macroporous spinel-type MCr₂O₄ (M = Co, Ni, Zn, Mn) catalysts with highly enhanced catalytic performance for soot combustion

KNO₃ supported on three-dimensionally ordered macroporous La_0.8Ce_0.2Mn_1−xFe_xO₃ for soot removal

Highly active MnO_x–CeO₂ catalyst for diesel soot combustion

Small-sized and high-dispersed WN from [SiO₄(W₃O₉)₄]⁴⁻ clusters loading on GO-derived graphene as promising carriers for methanol electro-oxidation

Low-temperature selective catalytic reduction of NO_x with NH₃ over a manganese and cerium oxide/graphene composite prepared by a hydrothermal method

Preparation of silica supported ceria–lanthana solid solutions useful for synthesis of 4-methylpent-1-ene and dehydroacetic acid

MnO_x–CeO₂ supported on a three-dimensional and networked SBA-15 monolith for NO_x-assisted soot combustion

Macroporous SmMn₂O₅ mullite for NO_x-assisted soot combustion

Similar Documents

Facile synthesis of catalytically active CeO2 for soot combustion

Boosting soot combustion efficiencies over CuO–CeO2 catalysts with a 3DOM structure

Three-dimensionally ordered macroporous spinel-type MCr2O4 (M = Co, Ni, Zn, Mn) catalysts with highly enhanced catalytic performance for soot combustion

KNO3 supported on three-dimensionally ordered macroporous La0.8Ce0.2Mn1−xFexO3 for soot removal

Highly active MnOx–CeO2 catalyst for diesel soot combustion

Small-sized and high-dispersed WN from [SiO4(W3O9)4]4− clusters loading on GO-derived graphene as promising carriers for methanol electro-oxidation

Low-temperature selective catalytic reduction of NOx with NH3 over a manganese and cerium oxide/graphene composite prepared by a hydrothermal method

Preparation of silica supported ceria–lanthana solid solutions useful for synthesis of 4-methylpent-1-ene and dehydroacetic acid

MnOx–CeO2 supported on a three-dimensional and networked SBA-15 monolith for NOx-assisted soot combustion

Macroporous SmMn2O5 mullite for NOx-assisted soot combustion

Facile synthesis of catalytically active CeO₂ for soot combustion

Boosting soot combustion efficiencies over CuO–CeO₂ catalysts with a 3DOM structure

Three-dimensionally ordered macroporous spinel-type MCr₂O₄ (M = Co, Ni, Zn, Mn) catalysts with highly enhanced catalytic performance for soot combustion

KNO₃ supported on three-dimensionally ordered macroporous La_0.8Ce_0.2Mn_1−xFe_xO₃ for soot removal

Highly active MnO_x–CeO₂ catalyst for diesel soot combustion

Small-sized and high-dispersed WN from [SiO₄(W₃O₉)₄]⁴⁻ clusters loading on GO-derived graphene as promising carriers for methanol electro-oxidation

Low-temperature selective catalytic reduction of NO_x with NH₃ over a manganese and cerium oxide/graphene composite prepared by a hydrothermal method

MnO_x–CeO₂ supported on a three-dimensional and networked SBA-15 monolith for NO_x-assisted soot combustion

Macroporous SmMn₂O₅ mullite for NO_x-assisted soot combustion