NDLI: Polyimide lifetime under partial discharge aging: effects of temperature, pressure and humidity

Content Provider	IEEE Xplore Digital Library
Author	Sili, E. Cambronne, J.P. Naude, N. Khazaka, R.
Copyright Year	1994
Abstract	Recent aircraft designs increasingly use electrical systems with higher voltages. This can lead to the occurrence of partial discharges. Testing for these phenomena is relatively poorly documented in comparison with other standardized tests available for aerospace components. After having investigated the effect of temperature, pressure, and moisture on the partial discharge inception voltage as well as the discharge characteristics, we focused on the effect of these environmental parameters on the behaviour of the energy dissipated by the discharges and on polyimide film endurance during aging under partial discharge. The results show two different behaviours for the variation of energy dissipation along aging time related to environmental conditions. In fact, when a semi-conducting layer is formed in wet conditions due to the interaction between the gaseous by-products and the water molecules, a decrease in the energy measured was revealed. In addition, the relationship between the measured dissipated energy and the polyimide lifetime was investigated and did not present constant trends for the different aging conditions. While it is clear that the material endurance was energy dependent in dry conditions, it was shown that, even when the discharge energies were higher, an increase in the endurance of the dielectric was observed when the superficial semi-conducting layer was formed.
Sponsorship	National Natural Science Foundation of China (NSFC) Region Centre Ville de Tours Conseil General D'Indre et Loire ABB IEEE Sandia National Laboratories TOSHIBA
Starting Page	435
Ending Page	442
Page Count	8
File Size	639948
File Format	PDF
ISSN	10709878
Volume Number	20
Issue Number	2
Language	English
Publisher	Institute of Electrical and Electronics Engineers, Inc. (IEEE)
Publisher Date	2013-01-01
Publisher Place	U.S.A.
Access Restriction	One Nation One Subscription (ONOS)
Rights Holder	Institute of Electrical and Electronics Engineers, Inc. (IEEE)
Subject Keyword	Partial discharges Aging Temperature measurement Polyimides Humidity Discharges (electric) Insulation anddissipated energy partial discharge polyimide film lifetime
Content Type	Text
Resource Type	Article
Subject	Electrical and Electronic Engineering

Sl.	Authority	Responsibilities	Communication Details
1	Ministry of Education (GoI), Department of Higher Education	Sanctioning Authority	https://www.education.gov.in/ict-initiatives
2	Indian Institute of Technology Kharagpur	Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project	https://www.iitkgp.ac.in
3	National Digital Library of India Office, Indian Institute of Technology Kharagpur	The administrative and infrastructural headquarters of the project	Dr. B. Sutradhar bsutra@ndl.gov.in
4	Project PI / Joint PI	Principal Investigator and Joint Principal Investigators of the project	Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon
5	Website/Portal (Helpdesk)	Queries regarding NDLI and its services	support@ndl.gov.in
6	Contents and Copyright Issues	Queries related to content curation and copyright issues	content@ndl.gov.in
7	National Digital Library of India Club (NDLI Club)	Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach	clubsupport@ndl.gov.in
8	Digital Preservation Centre (DPC)	Assistance with digitizing and archiving copyright-free printed books	dpc@ndl.gov.in
9	IDR Setup or Support	Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops	idr@ndl.gov.in

Effect of direct fluorination on surface partial discharge characteristics of polyimide films

Microscopic view of aging mechanism of polyimide film under pulse voltage in presence of partial discharge

Degradation mechanism of A1₂O₃ nano filled polyimide film due to surface discharge under square impulse voltage

Contribution of humidity to the evolution of slot partial discharges

Experiment and modeling of void discharges within dielectric insulation material under impulse voltage

New high temperature polyimide insulation for partial discharge resistance in harsh environments

Fillers in insulation for rotating electrical machines

Influence of inorganic nano-filler to partial discharge of polyimide film under high-frequency impulses

AC breakdown strength of aromatic polymers under partial discharge reducing conditions

Polyimide lifetime under partial discharge aging: effects of temperature, pressure and humidity

Similar Documents

Effect of direct fluorination on surface partial discharge characteristics of polyimide films

Microscopic view of aging mechanism of polyimide film under pulse voltage in presence of partial discharge

Degradation mechanism of A12O3 nano filled polyimide film due to surface discharge under square impulse voltage

Contribution of humidity to the evolution of slot partial discharges

Experiment and modeling of void discharges within dielectric insulation material under impulse voltage

New high temperature polyimide insulation for partial discharge resistance in harsh environments

Fillers in insulation for rotating electrical machines

Influence of inorganic nano-filler to partial discharge of polyimide film under high-frequency impulses

AC breakdown strength of aromatic polymers under partial discharge reducing conditions

Polyimide lifetime under partial discharge aging: effects of temperature, pressure and humidity

Degradation mechanism of A1₂O₃ nano filled polyimide film due to surface discharge under square impulse voltage