Addition of silicon improves oxidation resistance of nickel based superalloys
| Content Provider | NASA Technical Reports Server (NTRS) |
|---|---|
| Author | Lowell Jr., C. E.Jr.,Miner, R. V. |
| Copyright Year | 1974 |
| Description | Specific weight changes of nickel-base superalloy B-1900 and B-1900 + 1% Si specimens were tested at 1273 K. B-1900 was losing weight at an increasing rate due to spalling of oxide scale while B-1900 + 1% Si was still gaining weight at low, nearly constant rate. Similar comparison in weight change was observed for specimens tested at 1373 K. |
| File Size | 107987 |
| Page Count | 2 |
| File Format | |
| Alternate Webpage(s) | http://archive.org/details/NASA_NTRS_Archive_19740000007 |
| Archival Resource Key | ark:/13960/t07x1548c |
| Language | English |
| Publisher Date | 1974-03-01 |
| Access Restriction | Open |
| Subject Keyword | Materials Aluminum Alloys Oxidation Resistance Nickel Alloys Siliconizing Heat Resistant Alloys Refractory Metal Alloys Ntrs Nasa Technical Reports ServerĀ (ntrs) Nasa Technical Reports Server Aerodynamics Aircraft Aerospace Engineering Aerospace Aeronautic Space Science |
| Content Type | Text |
| Resource Type | Technical Report |