Improvement in cyclic oxidation of the nickel-base superalloy b-1900 by addition of one percent silicon
| Content Provider | NASA Technical Reports Server (NTRS) |
|---|---|
| Author | Lowell, C. E. Miner, R. V. |
| Copyright Year | 1973 |
| Description | Cast B-1900 with and without 1 weight percent Si was subjected to cyclic oxidation at 1000 and 1100 C in air for 700 and 200 hours, respectively. The results were judged by specific weight change, metallography and X-ray diffraction. Si was found to be of significant value in reducing oxidation attack, probably by increasing scale adherence. |
| File Size | 2177003 |
| Page Count | 14 |
| File Format | |
| Alternate Webpage(s) | http://archive.org/details/NASA_NTRS_Archive_19730007837 |
| Archival Resource Key | ark:/13960/t92853f51 |
| Language | English |
| Publisher Date | 1973-01-18 |
| Access Restriction | Open |
| Subject Keyword | Materials, Metallic Metallography Oxidation Silicon Nickel Alloys X Ray Diffraction Heat Resistant Alloys Ntrs Nasa Technical Reports Server (ntrs) Nasa Technical Reports Server Aerodynamics Aircraft Aerospace Engineering Aerospace Aeronautic Space Science |
| Content Type | Text |
| Resource Type | Technical Report |