NDLI: Analysis of Accelerated Exposure Testing of Thin-Glass Mirror Matrix

Content Provider	The American Society of Mechanical Engineers (ASME) Digital Collection
Author	Kennedy, C. E. Terwilliger, K. Jorgensen, G. J.
Copyright Year	2005
Abstract	Concentrating solar power (CSP) companies have deployed thin-glass mirrors produced by wet silver processes on ∼1-mm-thick, relatively lightweight glass. These mirrors have been bonded to metal substrates in commercial installations. Initial hemispherical reflectance is ∼93% to 96%, and the cost is ∼$16.1/m2 to $43.0/m2. These mirrors have the confidence of the CSP industry. However, corrosion was observed in mirror elements of operational solar systems deployed outdoors for 2 years. NREL’s advanced optical materials team was assigned to investigate the problem. First, it was noted that this corrosion is very similar to the corrosion bands and spots observed on small (45 mm × 67 mm) thin-glass mirrors laminated to metal substrates with several different types of adhesives and subjected to accelerated exposure testing (AET) at NREL. These samples exhibited corrosion at the unprotected edges and along cracks, and the choice of adhesive affected the performance of weathered thin-glass mirrors. Secondly, two significant changes in mirror manufacture have occurred in the wet-chemistry process because of environmental concerns. The first is the method of forming a copper-free reflective mirror, and the second is the use of lead-free paints. A test matrix of 84 combinations of sample constructions (mirror type / back protective paint / adhesive / substrate) was devised for AET as a designed experiment to identify the most promising mirrors, paints, and adhesives for use with concentrator designs. Two types of accelerated exposure were used: an Atlas Ci5000 WeatherOmeter (WOM) and a damp-heat chamber. Based on an analysis of variance (ANOVA), the various factors and interactions were modeled. These samples now have almost 24 months of accelerated exposure. Analysis of the thin-glass mirror matrix indicated that the Glaverbel mirror with a copperless formulation demonstrates slightly better performance compared to the Naugatuck standard copper-containing mirror and new copperless constructions although most results are within experimental uncertainty. Analysis of the thin-glass mirror matrix indicates commercial (non-mirror) back-protective paint applied after mirror manufacturing is not beneficial. Degradation of the samples exposed to date in the damp-heat chamber is similar, but at a rate 10 times faster than observed for samples in the WOM. We will discuss the results of the continued exposure testing of these mirror samples. Although glass mirrors with copper back-layers and heavily leaded paints have been considered robust for outdoor use, the new copperless back-layer and lead-free paint systems were designed for interior mirror applications and the outdoor durability must be determined.
Sponsorship	Solar Energy Division
Starting Page	757
Ending Page	763
Page Count	7
File Format	PDF
ISBN	0791847373
DOI	10.1115/ISEC2005-76040
e-ISBN	0791837653
Volume Number	Solar Energy
Conference Proceedings	ASME 2005 International Solar Energy Conference
Language	English
Publisher Date	2005-08-06
Publisher Place	Orlando, Florida, USA
Access Restriction	Subscribed
Subject Keyword	Mirror Copperless Lead-free paint Thin-glass Mirrors Glass Testing
Content Type	Text
Resource Type	Article

Sl.	Authority	Responsibilities	Communication Details
1	Ministry of Education (GoI), Department of Higher Education	Sanctioning Authority	https://www.education.gov.in/ict-initiatives
2	Indian Institute of Technology Kharagpur	Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project	https://www.iitkgp.ac.in
3	National Digital Library of India Office, Indian Institute of Technology Kharagpur	The administrative and infrastructural headquarters of the project	Dr. B. Sutradhar bsutra@ndl.gov.in
4	Project PI / Joint PI	Principal Investigator and Joint Principal Investigators of the project	Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon
5	Website/Portal (Helpdesk)	Queries regarding NDLI and its services	support@ndl.gov.in
6	Contents and Copyright Issues	Queries related to content curation and copyright issues	content@ndl.gov.in
7	National Digital Library of India Club (NDLI Club)	Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach	clubsupport@ndl.gov.in
8	Digital Preservation Centre (DPC)	Assistance with digitizing and archiving copyright-free printed books	dpc@ndl.gov.in
9	IDR Setup or Support	Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops	idr@ndl.gov.in