| Author | Fang, B. Y. Wang, J. Q. Han, E. -H Zhu, Z. Y. Ke, W. |
| Copyright Year | 2004 |
| Abstract | Stress corrosion cracking behavior of X70 pipeline steel was studied using slow strain rate tests (SSRT) and cyclic loading at high R and low frequency in a nearneutral pH soil solution saturated with 5% CO2+95% N2. The soil was from Xinjiang Uygur Autonomous Region where the Chinese West-East natural gas transmission pipeline started. Electrochemical tests including a potentiodynamic polarization technique and electrochemical impedance spectrum (EIS) were also conducted in order to analyze the effect of the concentration of bicarbonate, bubbled gas and the addition of chloride ion on the polarization behaviors. The results of SSRT showed that transgranular stress corrosion cracking (TGSCC) occurred in Xinjiang soil solution. Crack initiation was associated with pitting, inclusion and streamline of rolling. The susceptibility to SCC increased with the decrease of the applied electrochemical potential and strain rate. Cyclic loading tests with smooth specimens showed that some cracks initiated after certain cycles and cracking mode was transgranular. Under the cyclic loading of high R and low frequency, the crack propagation rate (CPR) of precracked specimens did not increase at some region of stress intensity factor range (ΔK), which showed that the crack propagation process was dominated by SCC. The results of the electrochemical tests showed that the polarization behaviors were influenced greatly by the concentration of bicarbonate, bubbled gas and the addition of chloride ion. Low concentration of chloride ion in bicarbonate could cause the elimination of passivity and SCC behavior to that in near-neutral pH soil solution. |
| Sponsorship | International Petroleum Technology Institute |
| Starting Page | 167 |
| Ending Page | 174 |
| Page Count | 8 |
| File Format | |
| ISBN | 0791841766 |
| DOI | 10.1115/IPC2004-0124 |
| e-ISBN | 0791837378 |
| Volume Number | 2004 International Pipeline Conference, Volumes 1, 2, and 3 |
| Conference Proceedings | 2004 International Pipeline Conference |
| Language | English |
| Publisher Date | 2004-10-04 |
| Publisher Place | Calgary, Alberta, Canada |
| Access Restriction | Subscribed |
| Subject Keyword | Cracking (materials) Cycles Electrochemical analysis Pipelines Carbon dioxide Stress corrosion cracking Fracture (materials) Steel Polarization (waves) Stress Polarization (electricity) Crack propagation Fracture (process) Polarization (light) Soil Natural gas Electrochemical impedance spectroscopy |
| Content Type | Text |
| Resource Type | Article |
National Digital Library of India (NDLI) is a virtual repository of learning resources which is not just a repository with search/browse facilities but provides a host of services for the learner community. It is sponsored and mentored by Ministry of Education, Government of India, through its National Mission on Education through Information and Communication Technology (NMEICT). Filtered and federated searching is employed to facilitate focused searching so that learners can find the right resource with least effort and in minimum time. NDLI provides user group-specific services such as Examination Preparatory for School and College students and job aspirants. Services for Researchers and general learners are also provided. NDLI is designed to hold content of any language and provides interface support for 10 most widely used Indian languages. It is built to provide support for all academic levels including researchers and life-long learners, all disciplines, all popular forms of access devices and differently-abled learners. It is designed to enable people to learn and prepare from best practices from all over the world and to facilitate researchers to perform inter-linked exploration from multiple sources. It is developed, operated and maintained from Indian Institute of Technology Kharagpur.
Learn more about this project from here.
NDLI is a conglomeration of freely available or institutionally contributed or donated or publisher managed contents. Almost all these contents are hosted and accessed from respective sources. The responsibility for authenticity, relevance, completeness, accuracy, reliability and suitability of these contents rests with the respective organization and NDLI has no responsibility or liability for these. Every effort is made to keep the NDLI portal up and running smoothly unless there are some unavoidable technical issues.
Ministry of Education, through its National Mission on Education through Information and Communication Technology (NMEICT), has sponsored and funded the National Digital Library of India (NDLI) project.
| Sl. | Authority | Responsibilities | Communication Details |
|---|---|---|---|
| 1 | Ministry of Education (GoI), Department of Higher Education |
Sanctioning Authority | https://www.education.gov.in/ict-initiatives |
| 2 | Indian Institute of Technology Kharagpur | Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project | https://www.iitkgp.ac.in |
| 3 | National Digital Library of India Office, Indian Institute of Technology Kharagpur | The administrative and infrastructural headquarters of the project | Dr. B. Sutradhar bsutra@ndl.gov.in |
| 4 | Project PI / Joint PI | Principal Investigator and Joint Principal Investigators of the project |
Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon |
| 5 | Website/Portal (Helpdesk) | Queries regarding NDLI and its services | support@ndl.gov.in |
| 6 | Contents and Copyright Issues | Queries related to content curation and copyright issues | content@ndl.gov.in |
| 7 | National Digital Library of India Club (NDLI Club) | Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach | clubsupport@ndl.gov.in |
| 8 | Digital Preservation Centre (DPC) | Assistance with digitizing and archiving copyright-free printed books | dpc@ndl.gov.in |
| 9 | IDR Setup or Support | Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops | idr@ndl.gov.in |
|
Loading...
|