| Abstract | The fluoride Ion cleaning (FIC) process is used to assist in the successful braze repair of nickel-based superalloy components. This process is especially effective in removing embedded oxides in cracks typically found in aircraft parts such as in combustors and turbine blades and vanes. Where, Al and Ti are present in the base metal, the FIC process depletes these elements from the surface, thereby improving the braze flow and repair of the cracked components. The objective of this paper is to show that mechanical properties of the braze repaired region can be adequate when the FIC process at sub-atmospheric pressure is utilized, prior to brazing. To achieve this, firstly entailed designing and producing specimens suitable to study the fatigue crack behavior of braze repaired cracks/joints under mechanical and thermal loading. The cracks/joints prior to brazing were either in an unclean form i.e. had an oxide layer on, or were fluoride ion cleaned at sub-atmospheric pressure. Fatigue crack propagation tests under constant load as well as under constant stress intensity factor range were conducted in order to study fatigue crack growth characteristics in the parent and braze repaired area. In addition, the resistance to thermal cycling was investigated using single-edge wedge specimens containing braze repaired joints. For the unclean crack specimens, abnormally high crack growth rates were obtained from the brazed repaired area as compared to parent Ni-based material; whereas for the fluoride ion cleaned crack specimens, lower crack growth rates were experienced. Similarly for the unclean crack specimens, the thermal fatigue crack initiation life was significantly shorter compared with the fluoride ion cleaned crack specimens. |
| Sponsorship | International Gas Turbine Institute |
| File Format | |
| ISBN | 9780791878576 |
| DOI | 10.1115/2000-GT-0338 |
| Volume Number | Volume 4: Manufacturing Materials and Metallurgy; Ceramics; Structures and Dynamics; Controls, Diagnostics and Instrumentation; Education |
| Conference Proceedings | ASME Turbo Expo 2000: Power for Land, Sea, and Air |
| Language | English |
| Publisher Date | 2000-05-08 |
| Publisher Place | Munich, Germany |
| Access Restriction | Subscribed |
| Subject Keyword | Turbine blades Mechanical properties Brazing Fracture (materials) Maintenance Superalloys Wedges Pressure Flow (dynamics) Stress Base metals Design Nickel Combustion chambers Aircraft Fatigue cracks |
| Content Type | Text |
| Resource Type | Article |
National Digital Library of India (NDLI) is a virtual repository of learning resources which is not just a repository with search/browse facilities but provides a host of services for the learner community. It is sponsored and mentored by Ministry of Education, Government of India, through its National Mission on Education through Information and Communication Technology (NMEICT). Filtered and federated searching is employed to facilitate focused searching so that learners can find the right resource with least effort and in minimum time. NDLI provides user group-specific services such as Examination Preparatory for School and College students and job aspirants. Services for Researchers and general learners are also provided. NDLI is designed to hold content of any language and provides interface support for 10 most widely used Indian languages. It is built to provide support for all academic levels including researchers and life-long learners, all disciplines, all popular forms of access devices and differently-abled learners. It is designed to enable people to learn and prepare from best practices from all over the world and to facilitate researchers to perform inter-linked exploration from multiple sources. It is developed, operated and maintained from Indian Institute of Technology Kharagpur.
Learn more about this project from here.
NDLI is a conglomeration of freely available or institutionally contributed or donated or publisher managed contents. Almost all these contents are hosted and accessed from respective sources. The responsibility for authenticity, relevance, completeness, accuracy, reliability and suitability of these contents rests with the respective organization and NDLI has no responsibility or liability for these. Every effort is made to keep the NDLI portal up and running smoothly unless there are some unavoidable technical issues.
Ministry of Education, through its National Mission on Education through Information and Communication Technology (NMEICT), has sponsored and funded the National Digital Library of India (NDLI) project.
| Sl. | Authority | Responsibilities | Communication Details |
|---|---|---|---|
| 1 | Ministry of Education (GoI), Department of Higher Education |
Sanctioning Authority | https://www.education.gov.in/ict-initiatives |
| 2 | Indian Institute of Technology Kharagpur | Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project | https://www.iitkgp.ac.in |
| 3 | National Digital Library of India Office, Indian Institute of Technology Kharagpur | The administrative and infrastructural headquarters of the project | Dr. B. Sutradhar bsutra@ndl.gov.in |
| 4 | Project PI / Joint PI | Principal Investigator and Joint Principal Investigators of the project |
Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon |
| 5 | Website/Portal (Helpdesk) | Queries regarding NDLI and its services | support@ndl.gov.in |
| 6 | Contents and Copyright Issues | Queries related to content curation and copyright issues | content@ndl.gov.in |
| 7 | National Digital Library of India Club (NDLI Club) | Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach | clubsupport@ndl.gov.in |
| 8 | Digital Preservation Centre (DPC) | Assistance with digitizing and archiving copyright-free printed books | dpc@ndl.gov.in |
| 9 | IDR Setup or Support | Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops | idr@ndl.gov.in |
|
Loading...
|