NDLI: Void Closure in a Large Cross Section Bars Hot Rolled from a Low Alloy Steel Ingot Casting

Content Provider	Springer Nature Link
Author	Nalawade, Rahul Shashikant Patil, Prafull Prataprao Balachandran, G. Balasubramanian, V.
Copyright Year	2016
Abstract	The void closure phenomenon of a large size rolled bar made from an as-cast low alloy steel ingot of grade AISI 4130 has been examined. The study involved FEM based simulation of hot rolling of a four metric ton ingot casting to a final product of 320 mm round corner square cross section with a reduction ratio of 4.3. The rolling process was varied at two process conditions. The process variables considered included initial cooling time of the ingot from soaking pit before rolling, rpm, reduction and pass schedule. The defects in the product at the two rolling conditions were experimentally evaluated using ultrasonic technique during hot rolling and compared with void fraction in the simulation. Higher initial time of cooling of the ingot before hot rolling, lower rpm, higher reduction and lesser number of tilts gave products with least core defect which justified simulation results. The study brought out at every stage the load and torque distribution, effective strain, stress triaxiality factor, void volume fraction and void healing hydrostatic integration parameter in the model which had enabled void closure.
Starting Page	1711
Ending Page	1721
Page Count	11
File Format	PDF
ISSN	09722815
Journal	Transactions of the Indian Institute of Metals
Volume Number	69
Issue Number	9
e-ISSN	09751645
Language	English
Publisher	Springer India
Publisher Date	2016-02-16
Publisher Place	New Delhi
Access Restriction	One Nation One Subscription (ONOS)
Subject Keyword	AISI 4130 Ingot hot rolling Simulation Porosity Pass schedule Void closure Hot rolling Ingot Metallic Materials Materials Science Tribology, Corrosion and Coatings
Content Type	Text
Resource Type	Article
Subject	Metals and Alloys

Sl.	Authority	Responsibilities	Communication Details
1	Ministry of Education (GoI), Department of Higher Education	Sanctioning Authority	https://www.education.gov.in/ict-initiatives
2	Indian Institute of Technology Kharagpur	Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project	https://www.iitkgp.ac.in
3	National Digital Library of India Office, Indian Institute of Technology Kharagpur	The administrative and infrastructural headquarters of the project	Dr. B. Sutradhar bsutra@ndl.gov.in
4	Project PI / Joint PI	Principal Investigator and Joint Principal Investigators of the project	Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon
5	Website/Portal (Helpdesk)	Queries regarding NDLI and its services	support@ndl.gov.in
6	Contents and Copyright Issues	Queries related to content curation and copyright issues	content@ndl.gov.in
7	National Digital Library of India Club (NDLI Club)	Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach	clubsupport@ndl.gov.in
8	Digital Preservation Centre (DPC)	Assistance with digitizing and archiving copyright-free printed books	dpc@ndl.gov.in
9	IDR Setup or Support	Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops	idr@ndl.gov.in

Microstructures and Textures of Hot Rolled and Hot Rolled-Normalized 2.9 % Silicon Steel Sheets

Corrosion Inhibition and Adsorption Behavior of Gentian Violet on AISI 4130 Alloy Steel in HCl Solution

Effects of NO$_{2}$ $^{−}$ and NO$_{3}$ $^{−}$ Ions on Corrosion of AISI 4130 Steel in Ethylene Glycol + Water Electrolyte

Fabrication and Characterization of Hot Rolled and Hot Extruded Boron Carbide (B$_{4}$C) Reinforced A356 Aluminum Alloy Matrix Composites Produced by Stir Casting Method

Influence of Welding Techniques on Heat Affected Zone Softening of Dissimilar Metal Maraging Steel and High Strength Low Alloy Steel Gas Tungsten Arc Weldments

On the hot tensile deformation behavior of an AISI 316LN stainless steel

Influence of Hot Rolling on Formability of Nb-Microalloyed Steel: An Experimental Design Study

Heat Flow and Solidification Modeling of Industrial Scale, Ingot Casting Operation

Microstructure and Texture Evolution During Annealing of Caliber Rolled Mg–3Al–1Zn Alloy

Void Closure in a Large Cross Section Bars Hot Rolled from a Low Alloy Steel Ingot Casting

Similar Documents

Microstructures and Textures of Hot Rolled and Hot Rolled-Normalized 2.9 % Silicon Steel Sheets

Corrosion Inhibition and Adsorption Behavior of Gentian Violet on AISI 4130 Alloy Steel in HCl Solution

Effects of NO$_{2}$ $^{−}$ and NO$_{3}$ $^{−}$ Ions on Corrosion of AISI 4130 Steel in Ethylene Glycol + Water Electrolyte

Fabrication and Characterization of Hot Rolled and Hot Extruded Boron Carbide (B$_{4}$C) Reinforced A356 Aluminum Alloy Matrix Composites Produced by Stir Casting Method

Influence of Welding Techniques on Heat Affected Zone Softening of Dissimilar Metal Maraging Steel and High Strength Low Alloy Steel Gas Tungsten Arc Weldments

On the hot tensile deformation behavior of an AISI 316LN stainless steel

Influence of Hot Rolling on Formability of Nb-Microalloyed Steel: An Experimental Design Study

Heat Flow and Solidification Modeling of Industrial Scale, Ingot Casting Operation

Microstructure and Texture Evolution During Annealing of Caliber Rolled Mg–3Al–1Zn Alloy

Void Closure in a Large Cross Section Bars Hot Rolled from a Low Alloy Steel Ingot Casting