NDLI: Microstructure, Precipitation, and Mechanical Properties of V-N-Alloyed Steel After Different Cooling Processes

Content Provider	Springer Nature Link
Author	Zhang, Jing Wang, Fu Ming Yang, Zhan Bing Li, Chang Rong
Copyright Year	2016
Abstract	Three cooling processes (direct air cooling, water cooling to 1023 K and 873 K (750 °C and 600 °C) followed by air cooling) after hot rolling are designed to develop V-N-alloyed 600 MPa grade high-strength steel for architectural construction. Microstructural characteristics, precipitation behavior, and mechanical properties were investigated. Experimental results indicate that all microstructures are composed of polygonal ferrite and pearlite. Compared to the microstructure obtained from traditional direct air cooling, the grain size of ferrite is refined from 6.5 to 4.6 μm and the interlamellar spacing of pearlite decreases from 136 to 45 nm, respectively, by the application of accelerated cooling and lower finish cooling temperature. The number fraction of high misorientation angle boundaries increases from 44 to 51 pct. Moreover, the sheet spacing of interphase precipitates decreases from (23 to 26 nm) to (14 to 17 nm) and the size of V(C,N) particles reduces from (5 to 8 nm) to (2 to 5 nm). Furthermore, the optimal mechanical properties are obtained in the steel water cooled to 873 K (600 °C), of which the yield strength, tensile strength, total elongation, uniform elongation, and impact energy at room temperature are 753 MPa, 922 MPa, 22 pct, 11 pct, and 36 J, respectively. Besides, the high yield strength is primarily attributed to the refined grains and precipitation hardening from interphase and random precipitation of nano-scale V(C,N) particles.
Starting Page	6621
Ending Page	6631
Page Count	11
File Format	PDF
ISSN	10735623
Journal	Metallurgical and Materials Transactions A
Volume Number	47
Issue Number	12
e-ISSN	15431940
Language	English
Publisher	Springer US
Publisher Date	2016-09-16
Publisher Place	New York
Access Restriction	One Nation One Subscription (ONOS)
Subject Keyword	Metallic Materials Characterization and Evaluation of Materials Structural Materials Surfaces and Interfaces, Thin Films Nanotechnology
Content Type	Text
Resource Type	Article
Subject	Mechanics of Materials Metals and Alloys Condensed Matter Physics

Sl.	Authority	Responsibilities	Communication Details
1	Ministry of Education (GoI), Department of Higher Education	Sanctioning Authority	https://www.education.gov.in/ict-initiatives
2	Indian Institute of Technology Kharagpur	Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project	https://www.iitkgp.ac.in
3	National Digital Library of India Office, Indian Institute of Technology Kharagpur	The administrative and infrastructural headquarters of the project	Dr. B. Sutradhar bsutra@ndl.gov.in
4	Project PI / Joint PI	Principal Investigator and Joint Principal Investigators of the project	Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon
5	Website/Portal (Helpdesk)	Queries regarding NDLI and its services	support@ndl.gov.in
6	Contents and Copyright Issues	Queries related to content curation and copyright issues	content@ndl.gov.in
7	National Digital Library of India Club (NDLI Club)	Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach	clubsupport@ndl.gov.in
8	Digital Preservation Centre (DPC)	Assistance with digitizing and archiving copyright-free printed books	dpc@ndl.gov.in
9	IDR Setup or Support	Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops	idr@ndl.gov.in

Microstructure and Properties of Nitrogen-Alloyed Martensitic Stainless Steel

Characterization of Microstructure and Mechanical Properties of 9.2Cr0.45V0.7C Heat-Resistant Steel

Effects of Ultra-Fast Cooling Technology on Microstructure and Properties of Low Carbon Steel

Microstructure and Mechanical Properties of a 18Kt 5N Gold Alloy After Different Heat Treatments

Microstructure and Mechanical Properties After Shock Wave Loading of Cast CrMnNi TRIP Steel

Microstructures and Properties of Copper to Stainless Steel Joints by Hybrid FSW

High-temperature Deformation Behavior of HP40Nb Micro-alloyed Reformer Steel

Microstructure and Mechanical Properties of a TRIP-Aided Martensitic Steel

Multilayer Mg-Stainless Steel Sheets, Microstructure, and Mechanical Properties

Microstructure, Precipitation, and Mechanical Properties of V-N-Alloyed Steel After Different Cooling Processes

Similar Documents

Microstructure and Properties of Nitrogen-Alloyed Martensitic Stainless Steel

Characterization of Microstructure and Mechanical Properties of 9.2Cr0.45V0.7C Heat-Resistant Steel

Effects of Ultra-Fast Cooling Technology on Microstructure and Properties of Low Carbon Steel

Microstructure and Mechanical Properties of a 18Kt 5N Gold Alloy After Different Heat Treatments

Microstructure and Mechanical Properties After Shock Wave Loading of Cast CrMnNi TRIP Steel

Microstructures and Properties of Copper to Stainless Steel Joints by Hybrid FSW

High-temperature Deformation Behavior of HP40Nb Micro-alloyed Reformer Steel

Microstructure and Mechanical Properties of a TRIP-Aided Martensitic Steel

Multilayer Mg-Stainless Steel Sheets, Microstructure, and Mechanical Properties

Microstructure, Precipitation, and Mechanical Properties of V-N-Alloyed Steel After Different Cooling Processes