WebSite Logo
  • Content
  • Similar Resources
  • Metadata
  • Cite This
  • Log-in
  • Fullscreen
Log-in
Do not have an account? Register Now
Forgot your password? Account recovery
  1. Journal of Wuhan University of Technology-Mater. Sci. Ed.
  2. Journal of Wuhan University of Technology-Mater. Sci. Ed. : Volume 31
  3. Journal of Wuhan University of Technology-Mater. Sci. Ed. : Volume 31, Issue 1, February 2016
  4. Galvanic corrosion of magnesium alloy and aluminum alloy by kelvin probe
Loading...

Please wait, while we are loading the content...

Journal of Wuhan University of Technology-Mater. Sci. Ed. : Volume 32
Journal of Wuhan University of Technology-Mater. Sci. Ed. : Volume 31
Journal of Wuhan University of Technology-Mater. Sci. Ed. : Volume 31, Issue 6, December 2016
Journal of Wuhan University of Technology-Mater. Sci. Ed. : Volume 31, Issue 5, October 2016
Journal of Wuhan University of Technology-Mater. Sci. Ed. : Volume 31, Issue 4, August 2016
Journal of Wuhan University of Technology-Mater. Sci. Ed. : Volume 31, Issue 3, June 2016
Journal of Wuhan University of Technology-Mater. Sci. Ed. : Volume 31, Issue 2, April 2016
Journal of Wuhan University of Technology-Mater. Sci. Ed. : Volume 31, Issue 1, February 2016
A review: Structural oxide coatings by laser chemical vapor deposition
Synthesis of sodium beta alumina films by heat treatment of sodium aluminum oxides
Development of electrospray laser chemical vapour deposition for homogenous alumina coatings
Morphology study of oriented SmBCO film deposited by MOCVD
Comprehensive optimization of electrical and optical properties for ATO films prepared by pulsed laser deposition
Effect of oxygen partial pressure on epitaxial growth and properties of laser-ablated AZO thin films
Effects of annealing processes on Cu$_{ x }$Si$_{1-x }$ thin films
Mechanistic investigation into the role of aluminum diffusion in the oxidation behavior of cryomilled NiCrAlY bond coat
Effect of substrate temperature on the structure and magnetic properties of CoPt/AlN multilayer films
Preparation, characterization and electronic properties of fluorine-doped tin oxide films
P-doped germanium nanowires with Fano-broadening in Raman spectrum
Influence of coal fly ash particle size on structure and adsorption properties of forming adsorbents for Cr$^{6+}$
Synthesis, structural characterization and hydrogen storage of nickel-containing mesoporous MCM-48 by electroless plating
Effect of pH on crystallization of nanocrystalline zirconia in a microwave-hydrothermal process
First-principles study of the high-temperature behaviors of the willemite-II and post-phenacite phases of silicon nitride
Structural characteristics and photocatalytic activity of ambient pressure dried SiO$_{2}$/TiO$_{2}$ aerogel composites by one-step solvent exchange/surface modification
Carrier transport across grain boundaries in polycrystalline silicon thin film transistors
Effect of wafer size on the film internal stress measurement by wafer curvature method
Kubelka-Munk revised theory for high solar reflectance and high long-wave emissivity coatings designing
Surface modification of natural fibrous brucite with stearic acid
Preparation of ordered mesoporous nanocrystalline ceria and ceria-zirconia for soot oxidation
Ballistic performance and damage characteristics of chemical vapor infiltration quasi 3D-Cf/SiC composites
Multi-scale modeling of the ionic diffusivity of cement-based materials
The competitive adsorption characteristics of welan gum and superplasticizer in cement mortar
Effect of isobutyl-triethoxy-silane penetrative protective agent on the carbonation resistance of concrete
Effects of carbonation on micro structures of hardened cement paste
Synthesis and swelling behaviors of microcrystal muscovite composite superabsorbent by photopolymerization
Kinetic study of thermal polymerization reactions between diazide and different diynes
Preparation and properties of heat resistant polylactic acid (PLA)/Nano-SiO$_{2}$ composite filament
CFRP voids 3D identification and location method based on the process of backscattered signal
Effect of direct quenching and partitioning treatment on mechanical properties of a hot rolled strip steel
Formation and mechanical properties of Zr-Nb-Cu-Ni-Al-Lu bulk glassy alloys with superior glass-forming ability
Crystallization kinetics of a high-zirconium-based glassy alloy: A DSC study
Mechanical and thermal expansion properties of SiC$_{p}$/ZAlSi9Mg composites produced by centrifugal casting
Galvanic corrosion of magnesium alloy and aluminum alloy by kelvin probe
Preparation, rheological properties and primary cytocompatibility of TPU/PLA blends as biomedical materials
Composition dependence of the thermal behavior, morphology and properties of biodegradable PBS/PTMO segment block copolymer
Morphology of barium hydrogen phosphate formation induced by phosphate-mineralization microbe
Journal of Wuhan University of Technology-Mater. Sci. Ed. : Volume 30
Journal of Wuhan University of Technology-Mater. Sci. Ed. : Volume 29
Journal of Wuhan University of Technology-Mater. Sci. Ed. : Volume 28
Journal of Wuhan University of Technology-Mater. Sci. Ed. : Volume 27
Journal of Wuhan University of Technology-Mater. Sci. Ed. : Volume 26
Journal of Wuhan University of Technology-Mater. Sci. Ed. : Volume 25
Journal of Wuhan University of Technology-Mater. Sci. Ed. : Volume 24
Journal of Wuhan University of Technology-Mater. Sci. Ed. : Volume 23
Journal of Wuhan University of Technology-Mater. Sci. Ed. : Volume 22
Journal of Wuhan University of Technology-Mater. Sci. Ed. : Volume 21
Journal of Wuhan University of Technology-Mater. Sci. Ed. : Volume 20
Journal of Wuhan University of Technology-Mater. Sci. Ed. : Volume 19
Journal of Wuhan University of Technology-Mater. Sci. Ed. : Volume 18
Journal of Wuhan University of Technology-Mater. Sci. Ed. : Volume 17

Similar Documents

...
Corrosion of carbon steel under epoxy-varnish coating studied by scanning Kelvin probe

Article

...
Application of aluminum coatings for the corrosion protection of magnesium by cold spray.

...
Experimental Investigation of the Corrosion Behavior of Friction Stir Welded AZ61A Magnesium Alloy Welds under Salt Spray Corrosion Test and Galvanic Corrosion Test Using Response Surface Methodology

Article

...
The Repair of Magnesium Rotorcraft Components by Cold Spray

Article

...
Molten Salt Corrosion Behavior of Dual-Phase High Entropy Alloy for Concentrating Solar Power Systems.

Article

...
Corrosion resistance of a new AL 6013-20 SiC(P) in salt spray chamber

Article

...
Corrosion of Calcium Phosphate Coated AZ31 Magnesium Alloy under a Salt Spray Test

Article

...
Corrosion fatigue behavior of the high-strength magnesium alloy AZ 80

Article

...
Comparative Evaluation of Corrosion Behavior of Friction Stir Welded AZ61A Magnesium Alloy Weldments in Immersion Corrosion Tests and Salt Spray Corrosion Tests Using Response Surface Methodology

Article

Galvanic corrosion of magnesium alloy and aluminum alloy by kelvin probe

Content Provider Springer Nature Link
Author Xiao, Kui Dong, Chaofang Wei, Dan Wu, Junsheng Li, Xiaogang
Copyright Year 2016
Abstract Galvanic corrosion on samples of AZ91D magnesium alloy coupled with 2A12 aluminum alloy during neutral salt spray test was investigated. The variations of the surface potential were measured using scanning kelvin probe (SKP). The results showed that galvanic effect on the corrosion of AZ91D magnesium alloy is closely related to the potential difference between the anodic and cathodic materials. In the initial period, corrosion only occurred in a narrow area at the coupling interface because of the limited distance galvanic current. Then, the corrosion rate of 2A12 aluminum alloy was accelerated due to its poor stability in strong alkali environment, which was attributed to the strong alkalization caused by the corrosion of AZ91D magnesium alloy. With the increase of the potential of 2A12 aluminum alloy as a result of the continuous covering of corrosion products, the potential difference between the two materials was enlarged, which enhanced the galvanic corrosion.
Starting Page 204
Ending Page 210
Page Count 7
File Format PDF
ISSN 10002413
Journal Journal of Wuhan University of Technology-Mater. Sci. Ed.
Volume Number 31
Issue Number 1
e-ISSN 19930437
Language English
Publisher Wuhan University of Technology
Publisher Date 2016-02-03
Publisher Place Wuhan
Access Restriction One Nation One Subscription (ONOS)
Subject Keyword magnesium alloy aluminum alloy galvanic corrosion scanning kelvin probe salt spray test Materials Science
Content Type Text
Resource Type Article
Subject Materials Science
  • About
  • Disclaimer
  • Feedback
  • Sponsor
  • Contact
  • Chat with Us
About National Digital Library of India (NDLI)
NDLI logo

National Digital Library of India (NDLI) is a virtual repository of learning resources which is not just a repository with search/browse facilities but provides a host of services for the learner community. It is sponsored and mentored by Ministry of Education, Government of India, through its National Mission on Education through Information and Communication Technology (NMEICT). Filtered and federated searching is employed to facilitate focused searching so that learners can find the right resource with least effort and in minimum time. NDLI provides user group-specific services such as Examination Preparatory for School and College students and job aspirants. Services for Researchers and general learners are also provided. NDLI is designed to hold content of any language and provides interface support for 10 most widely used Indian languages. It is built to provide support for all academic levels including researchers and life-long learners, all disciplines, all popular forms of access devices and differently-abled learners. It is designed to enable people to learn and prepare from best practices from all over the world and to facilitate researchers to perform inter-linked exploration from multiple sources. It is developed, operated and maintained from Indian Institute of Technology Kharagpur.

Learn more about this project from here.

Disclaimer

NDLI is a conglomeration of freely available or institutionally contributed or donated or publisher managed contents. Almost all these contents are hosted and accessed from respective sources. The responsibility for authenticity, relevance, completeness, accuracy, reliability and suitability of these contents rests with the respective organization and NDLI has no responsibility or liability for these. Every effort is made to keep the NDLI portal up and running smoothly unless there are some unavoidable technical issues.

Feedback

Sponsor

Ministry of Education, through its National Mission on Education through Information and Communication Technology (NMEICT), has sponsored and funded the National Digital Library of India (NDLI) project.

Contact National Digital Library of India
Central Library (ISO-9001:2015 Certified)
Indian Institute of Technology Kharagpur
Kharagpur, West Bengal, India | PIN - 721302
See location in the Map
03222 282435
Mail: support@ndl.gov.in
Sl. Authority Responsibilities Communication Details
1 Ministry of Education (GoI),
Department of Higher Education
Sanctioning Authority https://www.education.gov.in/ict-initiatives
2 Indian Institute of Technology Kharagpur Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project https://www.iitkgp.ac.in
3 National Digital Library of India Office, Indian Institute of Technology Kharagpur The administrative and infrastructural headquarters of the project Dr. B. Sutradhar  bsutra@ndl.gov.in
4 Project PI / Joint PI Principal Investigator and Joint Principal Investigators of the project Dr. B. Sutradhar  bsutra@ndl.gov.in
Prof. Saswat Chakrabarti  will be added soon
5 Website/Portal (Helpdesk) Queries regarding NDLI and its services support@ndl.gov.in
6 Contents and Copyright Issues Queries related to content curation and copyright issues content@ndl.gov.in
7 National Digital Library of India Club (NDLI Club) Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach clubsupport@ndl.gov.in
8 Digital Preservation Centre (DPC) Assistance with digitizing and archiving copyright-free printed books dpc@ndl.gov.in
9 IDR Setup or Support Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops idr@ndl.gov.in
I will try my best to help you...
Cite this Content
Loading...