NDLI: Evaluation of the Microporosity of Aluminium Pillared Montmorillonite: Optimisation of the Exchange Process

Content Provider	Springer Nature Link
Author	De Bock, M. Nijs, H. Cool, P. Vansant, E.F.
Copyright Year	1999
Abstract	Aluminium pillared clays were synthesised under various experimental conditions starting from a sodium montmorillonite clay (Hithix). The influence of sonication, successive exchange and a constant pH during and after the intercalation process were investigated as important synthesis parameters in the optimisation of these materials. The concentration of aluminium in the pillaring solution, the ratio of Al/clay and the aging time and temperature were kept constant throughout this work. This optimisation is necessary in order to obtain high-quality Al-PILCs, as could be deduced from a theoretical study on the potential and limitations of pillared clay substrates. The ultrasonic treatment of the suspension during the synthesis is responsible for a significant increase in porosity. Despite the promising nature of the successive exchange technique, a reduction of the porosity is observed. Instead of a homogenisation process, an accumulation of aluminium in the interlayer space occurred. This expected homogenisation takes place when the synthesis of the pillared clay was carried out at constant pH. In this case, nitrogen BET surface areas of 458 m$^{2}$/g and micropore volumes of 0.17 cm$^{3}$/g were obtained after calcination of the intercalated clays at 400°C.
Starting Page	323
Ending Page	333
Page Count	11
File Format	PDF
ISSN	13802224
Journal	Journal of Porous Materials
Volume Number	6
Issue Number	4
e-ISSN	15734854
Language	English
Publisher	Kluwer Academic Publishers
Publisher Date	1999-01-01
Publisher Place	Boston
Access Restriction	One Nation One Subscription (ONOS)
Subject Keyword	Physical Chemistry Catalysis Characterization and Evaluation Materials
Content Type	Text
Resource Type	Article
Subject	Mechanics of Materials Materials Science Mechanical Engineering

Sl.	Authority	Responsibilities	Communication Details
1	Ministry of Education (GoI), Department of Higher Education	Sanctioning Authority	https://www.education.gov.in/ict-initiatives
2	Indian Institute of Technology Kharagpur	Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project	https://www.iitkgp.ac.in
3	National Digital Library of India Office, Indian Institute of Technology Kharagpur	The administrative and infrastructural headquarters of the project	Dr. B. Sutradhar bsutra@ndl.gov.in
4	Project PI / Joint PI	Principal Investigator and Joint Principal Investigators of the project	Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon
5	Website/Portal (Helpdesk)	Queries regarding NDLI and its services	support@ndl.gov.in
6	Contents and Copyright Issues	Queries related to content curation and copyright issues	content@ndl.gov.in
7	National Digital Library of India Club (NDLI Club)	Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach	clubsupport@ndl.gov.in
8	Digital Preservation Centre (DPC)	Assistance with digitizing and archiving copyright-free printed books	dpc@ndl.gov.in
9	IDR Setup or Support	Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops	idr@ndl.gov.in

Theoretical Evaluation of the Microporosity of Pillared Layered Double Hydroxides

Porosity and Thermal Stability of Montmorillonite Pillared with Mixed Oxides of Lanthanum, Calcium and Aluminium

Hydroxylation of phenol over rare earth exchanged iron pillared montmorillonites

Synthesis of porous Al pillared montmorillonite after pre-intercalation with dodecylamine: textural and thermal properties

Synthesis and characterization of Cr-pillared clays: modelling using factorial design methodology

An improved route for the synthesis of Al$_{13}$-pillared montmorillonite catalysts

Preparation and characterization of mesoporous silica-pillared montmorillonite

Selective Methyl Tert-Butyl Ether Synthesis over Metal Exchanged Pillared Clays

Synthesis and Photocatalytic Activity of Titania Pillared Clays

Evaluation of the Microporosity of Aluminium Pillared Montmorillonite: Optimisation of the Exchange Process

Similar Documents

Theoretical Evaluation of the Microporosity of Pillared Layered Double Hydroxides

Porosity and Thermal Stability of Montmorillonite Pillared with Mixed Oxides of Lanthanum, Calcium and Aluminium

Hydroxylation of phenol over rare earth exchanged iron pillared montmorillonites

Synthesis of porous Al pillared montmorillonite after pre-intercalation with dodecylamine: textural and thermal properties

Synthesis and characterization of Cr-pillared clays: modelling using factorial design methodology

An improved route for the synthesis of Al$_{13}$-pillared montmorillonite catalysts

Preparation and characterization of mesoporous silica-pillared montmorillonite

Selective Methyl Tert-Butyl Ether Synthesis over Metal Exchanged Pillared Clays

Synthesis and Photocatalytic Activity of Titania Pillared Clays

Evaluation of the Microporosity of Aluminium Pillared Montmorillonite: Optimisation of the Exchange Process