NDLI: Comparison of the performance of natural latex membranes prepared with different procedures and PTFE membrane in guided bone regeneration (GBR) in rabbits

Content Provider	Springer Nature Link
Author	Moura, Jonas M. L. Ferreira, Juliana F. Marques, Leonardo Holgado, Leandro Graeff, Carlos F. O. Kishita, Angela
Copyright Year	2014
Abstract	This work assessed the performance of membranes made of natural latex extracted from Hevea brasiliensis prepared with three different methods: polymerized immediately after collection without the use of ammonia (L1); polymerized after preservation in ammonia solution (L2); and polymerized after storage in ammonia, followed by Soxhlet technique for the extraction of substances (L3). Polytetrafluoroethylene (PTFE) membrane was used as control. Two 10-mm diameter bone defects were surgically made in the calvaria of thirty adult male New Zealand rabbits. Defects (total n = 60) were treated with guided bone regeneration (GBR) using L1, L2, L3 or PTFE membranes (n = 15 for each membrane). Ten animals were euthanized after 7, 20 and 60 days postoperatively so that five samples (n = 5) of each treatment were collected at each time, and bone regeneration was assessed microscopically. The microscopic analysis revealed defects filled with blood clot and new bone formation at the margins of the defect in all 7-day samples, while 20-day defects were mainly filled with fibrous connective tissue. After 60 days defects covered with L1 membranes showed a significantly larger bone formation area in comparison to the other groups (P < 0.05, ANOVA, Tukey). Additionally, bone tissue hypersensitization for L1 and PTFE membranes was also investigated in six additional rabbits. The animals were subjected to the same surgical procedure for the confection of one 10-mm diameter bone defect that was treated with L1 (n = 3) or PTFE (n = 3). Fifty-three days later, a second surgery was performed to make a second defect, which was treated with the same type of membrane used in the first surgery. Seven days later, the animals were euthanized and samples analyzed. No differences among L1 and PTFE samples collected from sensitized and non-sensitized animals were found (P > 0.05, Kruskal–Wallis). Therefore, the results demonstrated that latex membranes presented performance comparable to PTFE membranes, and that L1 membranes induced higher bone formation. L1 and PTFE membranes produced no hypersensitization in the bone tissue.
Starting Page	2111
Ending Page	2120
Page Count	10
File Format	PDF
ISSN	09574530
Journal	Journal of Materials Science: Materials in Medicine
Volume Number	25
Issue Number	9
e-ISSN	15734838
Language	English
Publisher	Springer US
Publisher Date	2014-05-22
Publisher Place	Boston
Access Restriction	Subscribed
Subject Keyword	Biomaterials Biomedical Engineering Regenerative Medicine/Tissue Engineering Polymer Sciences Ceramics, Glass, Composites, Natural Methods Surfaces and Interfaces, Thin Films
Content Type	Text
Resource Type	Article
Subject	Biomaterials Biophysics Bioengineering Biomedical Engineering

Sl.	Authority	Responsibilities	Communication Details
1	Ministry of Education (GoI), Department of Higher Education	Sanctioning Authority	https://www.education.gov.in/ict-initiatives
2	Indian Institute of Technology Kharagpur	Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project	https://www.iitkgp.ac.in
3	National Digital Library of India Office, Indian Institute of Technology Kharagpur	The administrative and infrastructural headquarters of the project	Dr. B. Sutradhar bsutra@ndl.gov.in
4	Project PI / Joint PI	Principal Investigator and Joint Principal Investigators of the project	Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon
5	Website/Portal (Helpdesk)	Queries regarding NDLI and its services	support@ndl.gov.in
6	Contents and Copyright Issues	Queries related to content curation and copyright issues	content@ndl.gov.in
7	National Digital Library of India Club (NDLI Club)	Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach	clubsupport@ndl.gov.in
8	Digital Preservation Centre (DPC)	Assistance with digitizing and archiving copyright-free printed books	dpc@ndl.gov.in
9	IDR Setup or Support	Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops	idr@ndl.gov.in

Comparison of the performance of natural latex membranes prepared with different procedures and PTFE membrane in guided bone regeneration (GBR) in rabbits.

Enhanced bioactivity of polyvinylidene chloride films using argon ion bombardment for guided bone regeneration

Magnetic forces and magnetized biomaterials provide dynamic flux information during bone regeneration

Microsphere-based scaffolds encapsulating tricalcium phosphate and hydroxyapatite for bone regeneration

Preparation and characterization of fibrous chitosan-glued phosphate glass fiber scaffolds for bone regeneration

Surface chemistry and effects on bone regeneration of a novel biomimetic synthetic bone filler

Production of new 3D scaffolds for bone tissue regeneration by rapid prototyping

A new sheep model with automatized analysis of biomaterial-induced bone tissue regeneration

A glass polyalkenoate cement carrier for bone morphogenetic proteins

Comparison of the performance of natural latex membranes prepared with different procedures and PTFE membrane in guided bone regeneration (GBR) in rabbits

Similar Documents

Comparison of the performance of natural latex membranes prepared with different procedures and PTFE membrane in guided bone regeneration (GBR) in rabbits.

Enhanced bioactivity of polyvinylidene chloride films using argon ion bombardment for guided bone regeneration

Magnetic forces and magnetized biomaterials provide dynamic flux information during bone regeneration

Microsphere-based scaffolds encapsulating tricalcium phosphate and hydroxyapatite for bone regeneration

Preparation and characterization of fibrous chitosan-glued phosphate glass fiber scaffolds for bone regeneration

Surface chemistry and effects on bone regeneration of a novel biomimetic synthetic bone filler

Production of new 3D scaffolds for bone tissue regeneration by rapid prototyping

A new sheep model with automatized analysis of biomaterial-induced bone tissue regeneration

A glass polyalkenoate cement carrier for bone morphogenetic proteins

Comparison of the performance of natural latex membranes prepared with different procedures and PTFE membrane in guided bone regeneration (GBR) in rabbits