Abstract	The effects of thermal aging and H2O treatment on the physicochemical properties of BaO/Al2O3 (the NOx storage component in the lean NOx trap systems) were investigated by means of X-ray diffraction (XRD), BET, TEM/EDX and NO2 TPD. Thermal aging at 1000 °C for 10 h converted dispersed BaO/BaCO3 on Al2O3 into low surface area crystalline BaAl2O4. TEM/EDX and XRD analysis showed that H2O treatment at room temperature facilitated a dissolution/reprecipitation process, resulting in the formation of a highly crystalline BaCO3 phase segregated from the Al2O3 support. Crystalline BaCO3 was formed from conversion of both BaAl2O4 and a dispersed BaO/BaCO3 phase, initially present on the Al2O3 support material after calcinations at 1000 and 500 °C, respectively. Such a phase change proceeded rapidly for dispersed BaO/BaCO3/Al2O3 samples calcined at relatively low temperatures with large BaCO3 crystallites observed in XRD within 10 min after contacting the sample with water. Significantly, we also find that the change in barium phase occurs even at room temperature in an ambient atmosphere by contact of the sample with moisture in the air, although the rate is relatively slow. These phenomena imply that special care to prevent the water contact must be taken during catalyst synthesis/storage, and during realistic operation of Pt/BaO/Al2O3 NOx trap catalysts since both processes involve potential exposure of the material to CO2 and liquid and/or vapor H2O. Based on the results, a model that describes the behavior of Ba-containing species upon thermal aging and H2O treatment is proposed.
Starting Page	259
Ending Page	268
Page Count	10
File Format	PDF
ISSN	1011372X
Journal	Catalysis Letters
Volume Number	105
Issue Number	3-4
e-ISSN	1572879X
Language	English
Publisher	Kluwer Academic Publishers-Plenum Publishers
Publisher Date	2005-01-01
Publisher Place	New York
Access Restriction	One Nation One Subscription (ONOS)
Subject Keyword	BaO/Al2O3 BaAl2O4 lean NOx trap NO2 TPD NOx storage nitric oxide Physical Chemistry Industrial Chemistry/Chemical Engineering Pharmacy Catalysis
Content Type	Text
Resource Type	Article
Subject	Chemistry Catalysis

Sl.	Authority	Responsibilities	Communication Details
1	Ministry of Education (GoI), Department of Higher Education	Sanctioning Authority	https://www.education.gov.in/ict-initiatives
2	Indian Institute of Technology Kharagpur	Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project	https://www.iitkgp.ac.in
3	National Digital Library of India Office, Indian Institute of Technology Kharagpur	The administrative and infrastructural headquarters of the project	Dr. B. Sutradhar bsutra@ndl.gov.in
4	Project PI / Joint PI	Principal Investigator and Joint Principal Investigators of the project	Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon
5	Website/Portal (Helpdesk)	Queries regarding NDLI and its services	support@ndl.gov.in
6	Contents and Copyright Issues	Queries related to content curation and copyright issues	content@ndl.gov.in
7	National Digital Library of India Club (NDLI Club)	Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach	clubsupport@ndl.gov.in
8	Digital Preservation Centre (DPC)	Assistance with digitizing and archiving copyright-free printed books	dpc@ndl.gov.in
9	IDR Setup or Support	Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops	idr@ndl.gov.in

Promotional Effects of H2O Treatment on NO x Storage Over Fresh and Thermally Aged Pt–BaO/Al2O3 Lean NO x Trap Catalysts

The Effect of Hydrogen on the Storage of NOx Over Silver, Platinum and Barium Containing NSR Catalysts

NOx Adsorption and Reduction over LaMnO3 Based Lean NOx Trap Catalysts

Lean NOx Trap Chemistry Under Lean-Gasoline Exhaust Conditions: Impact of High NOx Concentrations and High Temperature

High-Temperature NOx Storage and Sulfur-Resistance of the Lithium-Based Lean-Burn NOx Trap Catalyst Pt/Li/TiO2–Al2O3

NO x uptake mechanism on Pt/BaO/Al2O3 catalysts

Enhanced Low Temperature NO$_{ x }$ Reduction Performance Over Bimetallic Pt/Rh–BaO Lean NO$_{ x }$ Trap Catalysts

Sulfation and Desulfation Mechanisms on Pt–BaO/Al2O3 NOx Storage-Reduction (NSR) Catalysts

Reduction of lean NOx by ethanol over Ag/Al2O3 catalysts in the presence of H2O and SO2

Changes in Ba Phases in BaO/Al2O3 upon Thermal Aging and H2O Treatment

Similar Documents

Promotional Effects of H2O Treatment on NO x Storage Over Fresh and Thermally Aged Pt–BaO/Al2O3 Lean NO x Trap Catalysts

The Effect of Hydrogen on the Storage of NOx Over Silver, Platinum and Barium Containing NSR Catalysts

NOx Adsorption and Reduction over LaMnO3 Based Lean NOx Trap Catalysts

Lean NOx Trap Chemistry Under Lean-Gasoline Exhaust Conditions: Impact of High NOx Concentrations and High Temperature

High-Temperature NOx Storage and Sulfur-Resistance of the Lithium-Based Lean-Burn NOx Trap Catalyst Pt/Li/TiO2–Al2O3

NO x uptake mechanism on Pt/BaO/Al2O3 catalysts

Enhanced Low Temperature NO$_{ x }$ Reduction Performance Over Bimetallic Pt/Rh–BaO Lean NO$_{ x }$ Trap Catalysts

Sulfation and Desulfation Mechanisms on Pt–BaO/Al2O3 NOx Storage-Reduction (NSR) Catalysts

Reduction of lean NOx by ethanol over Ag/Al2O3 catalysts in the presence of H2O and SO2

Changes in Ba Phases in BaO/Al2O3 upon Thermal Aging and H2O Treatment