| Content Provider | Springer Nature Link |
|---|---|
| Author | Sayar, F. Güven, G. Pişkin, E. |
| Copyright Year | 2005 |
| Abstract | Magnetically loaded polymeric nano-particles carrying functional groups on their surface were prepared by a two-stage process. In the first stage, super-paramagnetic magnetite (Fe3O4) nano-particles were produced by a co-precipitation method from the aqueous solutions of FeCl2·4H2O and FeCl3·6H2O using a NaOH solution. The smallest size obtained was 40.9 nm with poly-dispersity index of 0.194 obtained by using a Zeta Sizer. The effects of Fe2+/Fe3+ molar ratio, stirring rate, temperature, base concentration, and pH on the particle size/size distribution and stability of the dispersions were examined. Increasing the relative concentration of Fe2+ ion and decreasing the stirring rate and pH increased the particle size, while the concentration of NaOH and temperature did not change the particle size significantly. Polymer coating was achieved by emulsion polymerization at high surfactant to monomer ratio of methyl methacrylate (MMA) and acrylic acid which were used as comonomers (comonomer ratio: 90/10 weight) with high surfactant to monomer ratio. The surfactant and initiator were SDS and KPS, respectively. Nano-particles in the range of 115 and 300 nm in diameter were produced depending on recipe. Increasing the Fe3O4/monomer and surfactant/monomer ratios, the KPS concentration caused a decrease in the average diameter. Magnetic properties of the nano-particles were obtained by electron spin resonance and vibrating-sample magnetometer. Most of the polymer-coated nano-particles exhibited super paramagnetic behavior. |
| Starting Page | 965 |
| Ending Page | 978 |
| Page Count | 14 |
| File Format | |
| ISSN | 0303402X |
| Journal | Colloid and Polymer Science |
| Volume Number | 284 |
| Issue Number | 9 |
| e-ISSN | 14351536 |
| Language | English |
| Publisher | Springer-Verlag |
| Publisher Date | 2005-09-15 |
| Publisher Place | Berlin/Heidelberg |
| Access Restriction | One Nation One Subscription (ONOS) |
| Subject Keyword | Magnetite nano-particles Poly(methyl methacrylate-co-acrylic acid) Magnetically loaded polymeric nano-particles Emulsion polymerization Soft Matter, Complex Fluids Characterization and Evaluation Materials Polymer Sciences Physical Chemistry Food Science |
| Content Type | Text |
| Resource Type | Article |
| Subject | Colloid and Surface Chemistry Materials Chemistry Physical and Theoretical Chemistry Polymers and Plastics |
National Digital Library of India (NDLI) is a virtual repository of learning resources which is not just a repository with search/browse facilities but provides a host of services for the learner community. It is sponsored and mentored by Ministry of Education, Government of India, through its National Mission on Education through Information and Communication Technology (NMEICT). Filtered and federated searching is employed to facilitate focused searching so that learners can find the right resource with least effort and in minimum time. NDLI provides user group-specific services such as Examination Preparatory for School and College students and job aspirants. Services for Researchers and general learners are also provided. NDLI is designed to hold content of any language and provides interface support for 10 most widely used Indian languages. It is built to provide support for all academic levels including researchers and life-long learners, all disciplines, all popular forms of access devices and differently-abled learners. It is designed to enable people to learn and prepare from best practices from all over the world and to facilitate researchers to perform inter-linked exploration from multiple sources. It is developed, operated and maintained from Indian Institute of Technology Kharagpur.
Learn more about this project from here.
NDLI is a conglomeration of freely available or institutionally contributed or donated or publisher managed contents. Almost all these contents are hosted and accessed from respective sources. The responsibility for authenticity, relevance, completeness, accuracy, reliability and suitability of these contents rests with the respective organization and NDLI has no responsibility or liability for these. Every effort is made to keep the NDLI portal up and running smoothly unless there are some unavoidable technical issues.
Ministry of Education, through its National Mission on Education through Information and Communication Technology (NMEICT), has sponsored and funded the National Digital Library of India (NDLI) project.
| Sl. | Authority | Responsibilities | Communication Details |
|---|---|---|---|
| 1 | Ministry of Education (GoI), Department of Higher Education |
Sanctioning Authority | https://www.education.gov.in/ict-initiatives |
| 2 | Indian Institute of Technology Kharagpur | Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project | https://www.iitkgp.ac.in |
| 3 | National Digital Library of India Office, Indian Institute of Technology Kharagpur | The administrative and infrastructural headquarters of the project | Dr. B. Sutradhar bsutra@ndl.gov.in |
| 4 | Project PI / Joint PI | Principal Investigator and Joint Principal Investigators of the project |
Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon |
| 5 | Website/Portal (Helpdesk) | Queries regarding NDLI and its services | support@ndl.gov.in |
| 6 | Contents and Copyright Issues | Queries related to content curation and copyright issues | content@ndl.gov.in |
| 7 | National Digital Library of India Club (NDLI Club) | Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach | clubsupport@ndl.gov.in |
| 8 | Digital Preservation Centre (DPC) | Assistance with digitizing and archiving copyright-free printed books | dpc@ndl.gov.in |
| 9 | IDR Setup or Support | Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops | idr@ndl.gov.in |
|
Loading...
|