NDLI: Physikalische und mechanische Eigenschaften von thermisch modifiziertem juvenilem und adultem Schwarzkiefernholz

Content Provider	Springer Nature Link
Author	Bal, Bekir Cihad
Copyright Year	2013
Abstract	In this study, test samples of juvenile and mature black pine wood were treated for 3 h at temperatures of 140, 170, and 200 °C. Mass loss, density, equilibrium moisture content (EMC), modulus of rupture (MOR), modulus of elasticity, and impact bending strength (IB) of the separate samples were determined. The purpose of the tests was to determine how heat treatment at the three temperatures influenced the properties of the juvenile and mature wood. The results showed that heat treatment had greater effects on mass loss, EMC, and density of juvenile wood than of mature wood. The results also showed that heat treatment had lesser effects on the MOR, modulus of elasticity, and IB of juvenile wood than of mature wood. The results clearly indicated that heat treatment had different effects on the properties of juvenile and mature black pine wood.In dieser Studie wurden Prüfkörper aus juvenilem und adultem Schwarzkiefernholz bei Temperaturen von 140, 170 und 200 °C für eine Dauer von 3 Stunden behandelt und der Masseverlust, die Dichte, die Gleichgewichtsfeuchte, die Biegefestigkeit, der Elastizitätsmodul und die Schlagbiegefestigkeit wurden bestimmt. Ziel dieser Studie war es, zu ermitteln, inwieweit eine Wärmebehandlung bei den drei Temperaturen die Eigenschaften von juvenilem und adultem Holz beeinflusst. Die Ergebnisse zeigten, dass sich die Wärmebehandlung auf den Masseverlust, die Gleichgewichtsfeuchte und die Dichte von juvenilem Holz stärker auswirkt als bei adultem Holz, wohingegen die Biegefestigkeit, der Elastizitätsmodul und die Schlagbiegefestigkeit bei juvenilem Holz weniger stark beeinflusst wurde als bei adultem Holz. Die Ergebnisse zeigen deutlich, dass sich eine Wärmebehandlung auf die Eigenschaften von juvenilem und adultem Schwarzkiefernholz unterschiedlich auswirkt.
Starting Page	61
Ending Page	66
Page Count	6
File Format	PDF
ISSN	00183768
Journal	Holz als Roh- und Werkstoff
Volume Number	72
Issue Number	1
e-ISSN	1436736X
Language	German
Publisher	Springer Berlin Heidelberg
Publisher Date	2013-10-17
Publisher Place	Berlin/Heidelberg
Access Restriction	One Nation One Subscription (ONOS)
Subject Keyword	Wood Science & Technology Ceramics, Glass, Composites, Natural Methods Operating Procedures, Materials Treatment
Content Type	Text
Resource Type	Article
Subject	Materials Science Forestry

Sl.	Authority	Responsibilities	Communication Details
1	Ministry of Education (GoI), Department of Higher Education	Sanctioning Authority	https://www.education.gov.in/ict-initiatives
2	Indian Institute of Technology Kharagpur	Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project	https://www.iitkgp.ac.in
3	National Digital Library of India Office, Indian Institute of Technology Kharagpur	The administrative and infrastructural headquarters of the project	Dr. B. Sutradhar bsutra@ndl.gov.in
4	Project PI / Joint PI	Principal Investigator and Joint Principal Investigators of the project	Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon
5	Website/Portal (Helpdesk)	Queries regarding NDLI and its services	support@ndl.gov.in
6	Contents and Copyright Issues	Queries related to content curation and copyright issues	content@ndl.gov.in
7	National Digital Library of India Club (NDLI Club)	Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach	clubsupport@ndl.gov.in
8	Digital Preservation Centre (DPC)	Assistance with digitizing and archiving copyright-free printed books	dpc@ndl.gov.in
9	IDR Setup or Support	Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops	idr@ndl.gov.in

Physikalische und mechanische Eigenschaften von thermisch modifiziertem E. grandis Holz

Mechanische und physikalische Eigenschaften von in einem Hochdruckreaktor unter Sattdampfbedingungen bei 120, 150 und 180 °C thermisch modifiziertem Kiefernholz

Mechanische Eigenschaften von thermisch modifiziertem Buchenholz für tragende Bauteile

Eigenschaften von juvenilem und adultem nicht angezapftem und angezapftem Gummibaumholz

Mechanische und physikalische Eigenschaften von Faserplatten aus landwirtschaftlichen Rohstoffen

Einfluss von Kupfernanopartikeln auf die Permeabilität und physikalische und mechanische Eigenschaften von Spanplatten

Physikalische und mechanische Eigenschaften von mit Portlandzement verstärkten gipsgebundenen Spanplatten

Einfluss der Hitze-Druck-Dämpfung auf mechanische und physikalische Eigenschaften von Stieleiche

Physikalische und mechanische Eigenschaften von Furnierstreifenholz (OSL) aus einer asiatischen Bambusart (Dendrocalamus asper Backer)

Physikalische und mechanische Eigenschaften von thermisch modifiziertem juvenilem und adultem Schwarzkiefernholz

Similar Documents

Physikalische und mechanische Eigenschaften von thermisch modifiziertem E. grandis Holz

Mechanische und physikalische Eigenschaften von in einem Hochdruckreaktor unter Sattdampfbedingungen bei 120, 150 und 180 °C thermisch modifiziertem Kiefernholz

Mechanische Eigenschaften von thermisch modifiziertem Buchenholz für tragende Bauteile

Eigenschaften von juvenilem und adultem nicht angezapftem und angezapftem Gummibaumholz

Mechanische und physikalische Eigenschaften von Faserplatten aus landwirtschaftlichen Rohstoffen

Einfluss von Kupfernanopartikeln auf die Permeabilität und physikalische und mechanische Eigenschaften von Spanplatten

Physikalische und mechanische Eigenschaften von mit Portlandzement verstärkten gipsgebundenen Spanplatten

Einfluss der Hitze-Druck-Dämpfung auf mechanische und physikalische Eigenschaften von Stieleiche

Physikalische und mechanische Eigenschaften von Furnierstreifenholz (OSL) aus einer asiatischen Bambusart (Dendrocalamus asper Backer)

Physikalische und mechanische Eigenschaften von thermisch modifiziertem juvenilem und adultem Schwarzkiefernholz