Evaluation of surface roughness of microhybrid and nanofilled composites after pH-cycling and simulated toothbrushing.
| Content Provider | Semantic Scholar |
|---|---|
| Author | Penteado, Roberta Alves Pinto Moura Tonholo, Josealdo Júnior, José Ginaldo Da Silva Silva, Milton Fernando Andrade Queiróz, Celso Da Silva Cavalli, Vanessa Rego, Marcos Augusto Do Liporoni, Priscila Christiane Suzy |
| Copyright Year | 2010 |
| Abstract | AIM This study evaluated the surface roughness patterns of two resin-based composite restorative materials, a microhybrid (Filtek Z250, 3M ESPE) and a nanofilled (Filtek Supreme, 3M ESPE), subjected to a regimen that simulated dynamic pH-cycling and toothbrushing. METHODS AND MATERIALS Twelve standardized cylindrical specimens of each resin-based composite material were prepared, finished, and mechanically polished. The experimental units were submitted to a pH-cycling regimen followed by 50,000 toothbrushing cycles, after which the surface roughness was measured using an atomic force microscope (AFM). AFM surface roughness was evaluated at three intervals: (1) immediately after specimen preparation (baseline), (2) after pH-cycling, and (3) after simulated toothbrushing. The results were then analyzed using a split-plot design and followed by linear regression and a Tukey's test at a significance level of p<0.05. RESULTS The results obtained indicated that simulated toothbrushing provoked a remarkable increase in surface roughness for both types of composite resins tested (p=0.0031). However, pH-cycling did not alter the surface of the composite under the conditions of this experiment. CONCLUSION Based on the results obtained, it was concluded that simulated toothbrushing was capable of increasing the surface roughness of the microhybrid (Filtek Z250) and the nanofilled (Filtek Supreme) composites tested. CLINICAL SIGNIFICANCE Surface roughness of nanofilled and microhybrid composites is significantly increased after toothbrushing, although pH-cycling, as tested in this study, does not appear to affect the morphology of either composite material. |
| File Format | PDF HTM / HTML |
| DOI | 10.5005/jcdp-11-6-17 |
| PubMed reference number | 21203733 |
| Journal | Medline |
| Volume Number | 11 |
| Issue Number | 6 |
| Journal | The journal of contemporary dental practice |
| Alternate Webpage(s) | https://www.thejcdp.com/doi/pdf/10.5005/jcdp-11-6-17 |
| Alternate Webpage(s) | https://doi.org/10.5005/jcdp-11-6-17 |
| Language | English |
| Access Restriction | Open |
| Content Type | Text |
| Resource Type | Article |