Catalytic Cracking of n-Octane over H-ZSM-5 Catalysts: Effect of Calcination and Steam Treatment
| Content Provider | Semantic Scholar |
|---|---|
| Author | 이현주 신채호 최원춘 이철위 박용기 Lee, Hyunju Shin, Chae-Ho Choi, Won Choon Lee, Chul Wee Park, Yong Ki |
| Copyright Year | 2008 |
| Abstract | Catalytic cracking of n-octane was carried out over H-ZSM-5 zeolite catalysts after calcination with air and steaming with 100% steam in the temperature range of 550-750 o C for 24 h and compared with the results of thermal cracking. The increase of calcination and steaming temperature resulted in the decrease of surface area, pore volume, and strong acid sites, which was mainly caused by the dealumination of H-ZSM-5 framework. It was found by 27 Al and 29 Si MAS NMR that the dealumination was proceeded through the transformation process of tetrahedral framework Al→ penta-cordinated Al → octahedral framework Al and the phenomena was much more severe in steaming conditions than that of calcination. In the catalytic cracking of n-octane, as the temperatures of calcination and steaming were increased, the conversion of n-octane, the selectivity of light olefins and ethylene to propylene ratio were decreased due to the dealumination of framework aluminum resulting the loss of acidic strengths. The conversion, selectivity of light olefins and ethylene to propylene ratio reached almost to the level of thermal cracking after steaming at 750 o C for 24 h. |
| Starting Page | 291 |
| Ending Page | 300 |
| Page Count | 10 |
| File Format | PDF HTM / HTML |
| Volume Number | 46 |
| Alternate Webpage(s) | https://www.cheric.org/PDF/HHKH/HK46/HK46-2-0291.pdf |
| Language | English |
| Access Restriction | Open |
| Content Type | Text |
| Resource Type | Article |