Identification of Retained Austenite, Ferrite, Bainite and Martensite in the Microstructure of TRIP Steel

Content Provider	Semantic Scholar
Author	Mostafapour, Amir Ebrahimpour, Alireza Saied, Taib
Copyright Year	2016
Abstract	Transformation induced plasticity (TRIP) steels have a vast application in automotive industry because of theirhigh strength, high ductility and hence excellent energy absorption capacity. These characteristics of TRIPsteels are due to the existence of retained austenite in their microstructures in the ambient temperature, whichtransforms to the martensite phase during deformation. The microstructure of TRIP steel contains various phasesand in the past-published studies mainly the volume fraction of retained austenite was investigated and thereis not a quantitative comprehensive investigation about all phases in the microstructure of this steel. The maingoal in this study is a comprehensive qualitative and quantitative investigation in various phases of TRIP steelmicrostructure. Therefore, a TRIP steel with chemical composition of 0.2C+ 1.43Si+ 1.58Mn was produced andits complicated microstructure which contained ferrite, bainite, martensite and retained austenite was investigatedusing X-Ray Diffractometry (XRD), optical microscopy (OM), field emission scanning microscopy (FE-SEM)and Electron backscatter diffraction (EBSD). The OM and FE-SEM results were used only to qualitative studiesand identification of the morphologies of the phases but the EBSD results and functions were used to qualitativeand quantitative studies. The volume fractions of retained austenite, ferrite+bainite and martensite phases werecalculated and the amounts of 11%, 82% and 7% were obtained, respectively. The volume fraction of retainedaustenite was also measured with XRD and the amount of 14.3% was obtained.
Starting Page	1
Ending Page	6
Page Count	6
File Format	PDF HTM / HTML
Volume Number	13
Alternate Webpage(s)	http://journal.issiran.com/article_23706_bdd6d21e6a5789c775d6d729a33f1a7e.pdf
Language	English
Access Restriction	Open
Content Type	Text
Resource Type	Article

Central Library (ISO-9001:2015 Certified)
Indian Institute of Technology Kharagpur
Kharagpur, West Bengal, India | PIN - 721302

See location in the Map
03222 282435
Mail: support@ndl.gov.in

Sl.	Authority	Responsibilities	Communication Details
1	Ministry of Education (GoI), Department of Higher Education	Sanctioning Authority	https://www.education.gov.in/ict-initiatives
2	Indian Institute of Technology Kharagpur	Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project	https://www.iitkgp.ac.in
3	National Digital Library of India Office, Indian Institute of Technology Kharagpur	The administrative and infrastructural headquarters of the project	Dr. B. Sutradhar bsutra@ndl.gov.in
4	Project PI / Joint PI	Principal Investigator and Joint Principal Investigators of the project	Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon
5	Website/Portal (Helpdesk)	Queries regarding NDLI and its services	support@ndl.gov.in
6	Contents and Copyright Issues	Queries related to content curation and copyright issues	content@ndl.gov.in
7	National Digital Library of India Club (NDLI Club)	Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach	clubsupport@ndl.gov.in
8	Digital Preservation Centre (DPC)	Assistance with digitizing and archiving copyright-free printed books	dpc@ndl.gov.in
9	IDR Setup or Support	Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops	idr@ndl.gov.in