Ultra-Large-Pore Mesoporous Carbons Templated from Poly(ethylene oxide)-b-Polystyrene Diblock Copolymer by Adding Polystyrene Homopolymer as a Pore Expander

Content Provider	Semantic Scholar
Author	Deng, Yonghui Liu, Chong Gu, Dong Sun, Zhenkun Wei, Jing Zhang, Junyong Zhang, Lijuan Zhao, Dongyuan
Copyright Year	2008
Abstract	A pore swelling approach was developed for the synthesis of ultralarge mesoporous carbons by using diblock copolymer PEO125-b-PS230 as a template, homopolystyrene (h-PS49) as a pore expander, resol as a carbon source, and THF as a solvent through solvent evaporation induced self-assembly (EISA). Small-angle X-ray scattering (SAXS) and transmission electron microscopy (TEM) characterizations show that when h-PS94 amount is lower than 20 wt% relative to PEO125-b-PS230, highly ordered face-center cubic (fcc) mesoporous carbon structure (space group Fm3m) with ultralarge cell parameter of 46.4−58.0 nm can be obtained. Nitrogen sorption measurements reveal that the obtained LP-FDU-18s possess high surface area of about 1210 m2/g and large pore volume of 1.10 cm3/g. Because of adding pore swelling agent h-PS49, the mesostructural shrinkage is restrained, the pore wall thickness becomes very thin (3.6 nm). With the increase of h-PS49 addition amount from 0 to 20 wt%, the pore size can be continuously tuned in t...
Starting Page	7281
Ending Page	7286
Page Count	6
File Format	PDF HTM / HTML
DOI	10.1021/cm802413q
Alternate Webpage(s)	https://liulab.seas.harvard.edu/files/jialiulab/files/dengetal2008_chemistry_of_materials.pdf
Alternate Webpage(s)	https://doi.org/10.1021/cm802413q
Volume Number	20
Language	English
Access Restriction	Open
Content Type	Text
Resource Type	Article