EVALUACIÓN DE HIDROGELES DE ACRILAMIDA-co-ÁCIDO ITACÓNICO EN LA DISMINUCIÓN DE IONES DE Fe CON POTENCIALES USOS EN PLANTAS PARA TRATAMIENTO DE AGUAS POTABILIZADAS
| Content Provider | Semantic Scholar |
|---|---|
| Author | Ramírez, Arnaldo Del Toro Astudillo, Henry Prin, José Luis Mora, Lenny Yojana Correa Gáscue, Blanca Rojas De |
| Copyright Year | 2012 |
| Abstract | En el siguiente trabajo se sintetizaron copolimeros hidrogeles (HGs) a partir de acrilamida con acido itaconico (AAm-co-AI) en agua desionizada. Se utilizo como iniciador persulfato de amonio (PSA) y como agente entrecruzante N,N`metilenbisacrilamida (NMBA). La determinacion del grado de hinchamiento (GH) se realizo gravimetricamente en agua desionizada y soluciones de FeSO 4 ∙3H 2 O, encontrandose que el GH presento una disminucion desde 9286 % en agua desionizada hasta 557 % en una solucion de 150 mg/L de Fe 2+ ; estas variaciones pueden ser explicadas en funcion del entrecruzamiento ionico generado y evaluando la formacion de complejos entre los grupos C=O y los iones hierro, que estarian sustituyendo a la formacion de los puentes de hidrogeno que se generan con el agua. Se estudio el efecto de la concentracion inicial de la solucion de FeSO 4 . 3H 2 O sobre la capacidad de absorcion de iones Fe 2+ en los hidrogeles sintetizados. Se prepararon soluciones con las siguientes concentraciones de Fe 2+ : 10 mg/L, 30 mg/L, 50 mg/L, 100 mg/L y 150 mg/L, encontrandose un incremento en la capacidad de absorcion a medida que se aumento la concentracion inicial de la solucion. Los resultados son relevantes porque dan indicios sobre las caracteristicas iniciales que debe tener el efluente a tratar para lograr la mayor absorcion posible de iones Fe 2+ , por parte del hidrogel de vista a su aplicacion en el tratamiento del agua para hacerla potable. In the following work copolymers hydrogels were synthesized from acrylamide with itaconic acid (AAm-co-AI) in deionized water. Persulphate ammonium (PSA) was used as initiator and N,N`-methylenebisacrylamide (NMBA) as crosslinking agent. Determining the degree of swelling (GH) was performed gravimetrically in deionized water and FeSO 4 . 3H 2 O solutions, finding that GH presented a decrease from 9286 % in deionized water to 557 % in a solution of 150 mg/L of Fe 2+ , these variations can be explained in terms of ionic crosslinking generated and evaluating the complex formation between C=O groups and Fe ions, which would be replacing the hydrogen bond formation with water. The effect of initial concentration of the FeSO 4 ∙3H 2 O solutions on the absorption capacity of Fe 2+ in synthesized hydrogels was studied. These solutions were prepared with the following concentrations of Fe 2+ : 10 mg/L, 30 mg/L, 50 mg/L, 100 mg/L y 150 mg/L found an increase in the absorption capacity when the initial concentration of solution was increased. The result are important because they give as evidence about the initial characteristics that must have the effluent to be treated to achieve the highest possible absorption of Fe 2+ ions in hydrogels, to its application in the treatment of water for drinking. |
| Starting Page | 32 |
| Ending Page | 35 |
| Page Count | 4 |
| File Format | PDF HTM / HTML |
| Alternate Webpage(s) | http://www.rlmm.org/ojs/index.php/rlmm/article/download/406/292 |
| Language | English |
| Access Restriction | Open |
| Content Type | Text |
| Resource Type | Article |