Epoxy nanocomposites filled with thermotropic liquid crystalline epoxy grafted graphene oxide

Content Provider	Semantic Scholar
Author	Lu, Shao-Rong Li, Shanrong Yu, Jinhong Yuan, Zhengkai
Copyright Year	2013
Abstract	Thermotropic liquid crystalline with epoxy groups grafted graphene oxide (LCE-g-GO) was synthesized by graphene oxide (GO), hexamethylene diisocyanate (HDI), and 4,4′-bis-(2-hydroxyhexoxy) biphenyl (BP2) by using pyridine and dibutyltin dilaurate as catalyst and dimethylformamide (DMF) as solvent. In this work, the LCE-g-GO nanosheets were characterized by Fourier transform infrared spectroscopy (FT-IR), wide angle X-ray diffraction (WAXD), differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), transmission electron microscopy (TEM) and polarizing optical microscopy (POM). The epoxy nanocomposites were fabricated by incorporating different LCE-g-GO loading using cast molding method. The results revealed that the incorporation of the LCE-g-GO resulted in a significant improvement in thermal and mechanical properties. The epoxy nanocomposite with 5 wt% LCE-g-GO produced an increase in the temperature for 5 wt% weight loss (T5%) by 47 °C and glass transition temperature (Tg) by 14 °C when compared with the neat epoxy. Moreover, at the addition of 5 wt% LCE-g-GO, the impact strength of the epoxy nanocomposite is 35.06 kJ m−2, which is 2 times higher than that of the neat epoxy resin (17.49 kJ m−2). Meanwhile, the tensile strength of the nanocomposite is significantly increased to 92.5 MPa from 54.3 MPa, while the elongation at break is also increased to 42.9% from 25.7% of the neat epoxy, respectively. Therefore, the presence of the LCE-g-GO in the epoxy matrix could make epoxy not only stronger but also tougher.
Starting Page	8915
Ending Page	8923
Page Count	9
File Format	PDF HTM / HTML
DOI	10.1039/C3RA40404H
Volume Number	3
Alternate Webpage(s)	http://www.rsc.org/suppdata/ra/c3/c3ra40404h/c3ra40404h.pdf
Alternate Webpage(s)	https://doi.org/10.1039/C3RA40404H
Language	English
Access Restriction	Open
Content Type	Text
Resource Type	Article

Central Library (ISO-9001:2015 Certified)
Indian Institute of Technology Kharagpur
Kharagpur, West Bengal, India | PIN - 721302

See location in the Map
03222 282435
Mail: support@ndl.gov.in

Sl.	Authority	Responsibilities	Communication Details
1	Ministry of Education (GoI), Department of Higher Education	Sanctioning Authority	https://www.education.gov.in/ict-initiatives
2	Indian Institute of Technology Kharagpur	Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project	https://www.iitkgp.ac.in
3	National Digital Library of India Office, Indian Institute of Technology Kharagpur	The administrative and infrastructural headquarters of the project	Dr. B. Sutradhar bsutra@ndl.gov.in
4	Project PI / Joint PI	Principal Investigator and Joint Principal Investigators of the project	Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon
5	Website/Portal (Helpdesk)	Queries regarding NDLI and its services	support@ndl.gov.in
6	Contents and Copyright Issues	Queries related to content curation and copyright issues	content@ndl.gov.in
7	National Digital Library of India Club (NDLI Club)	Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach	clubsupport@ndl.gov.in
8	Digital Preservation Centre (DPC)	Assistance with digitizing and archiving copyright-free printed books	dpc@ndl.gov.in
9	IDR Setup or Support	Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops	idr@ndl.gov.in