Structure and Magnetic Properties of Amorphous Fe 60 Co 10 Mo 2 W x Y 8 B 20 − x ( x = 0 , 1 ) Alloys
| Content Provider | Semantic Scholar |
|---|---|
| Author | Bloch, Klaus Nabiałek, Marcin Garus, Sebastian |
| Copyright Year | 2016 |
| Abstract | This paper presents studies of the bulk amorphous alloys: Fe60Co10Mo2Y8B20 and Fe60Co10Mo2W1Y8B19; both compounds were obtained by means of the injection-casting method in which liquid alloy is forced under pressure into a copper mould. The structure of the samples was studied using X-ray diffraction and scanning electron microscopy. Based on the results of the X-ray diffraction studies, it was found that the samples were in the amorphous state. Scanning electron microscopy image analysis of fractured alloy samples indicated the presence of areas of varying degrees of relaxation: “smooth”, “vein”, and “flake” fractures. The manufactured ferromagnetic samples were characterized by so-called soft magnetic properties with a relatively high Curie temperature of more than 520 K. In the investigated samples, the saturation magnetization was found to have been decreased from 1.14 T to 1.13 T after the addition of W. Tungsten also contributed significantly to an increase in the value of the coercive field, from 27 A/m to 8685 A/m. Following the addition of just 1% of W to the alloy, a substantial change was observed in the form of the static magnetic hysteresis loop: characterized by the so-called “wasp” shape. This result shows that an additional magnetically hard phase had appeared within the sample. |
| File Format | PDF HTM / HTML |
| Alternate Webpage(s) | http://przyrbwn.icm.edu.pl/APP/PDF/130/a130z4p25.pdf |
| Language | English |
| Access Restriction | Open |
| Content Type | Text |
| Resource Type | Article |