Alumina-Doped Silica Aerogels for High-Temperature Thermal Insulation
| Content Provider | MDPI |
|---|---|
| Author | Wu, Yu Wang, Xiaodong Liu, Lin Zhang, Ze Shen, Jun |
| Copyright Year | 2021 |
| Description | In this study, we used two methods to prepare alumina-doped silica aerogels with the aim of increasing the thermal stability of silica aerogels. The first method was physical doping of $α-Al_{2}O_{3}$ nano powders, and the second method was to create a chemical compound via the co-precursor of TEOS and $AlCl_{3}·6H_{2}$O in different proportions. The shrinkage, chemical composition, and specific surface area (SSA) of samples after heating at different temperatures were analyzed. Our results show that the silicon hydroxyl groups of samples derived from $AlCl_{3}·6H_{2}$O gradually decreased and nearly disappeared after heating at 800 °C, which indicates the complete dehydration of the silicon hydroxyl. Thus, the samples exhibited a large linear shrinkage and decreased SSA after high-temperature heat treatment. By contrast, samples doped with $α-Al_{2}O_{3}$ powders retained abundant silicon hydroxyl groups, and the 6.1 wt.% $α-Al_{2}O_{3}$-doped sample exhibited the lowest linear shrinkage of 11% and the highest SSA of 1056 $m^{2}$/g after heat treatment at 800 °C. The alumina-doped silica aerogels prepared using a simple and low-price synthesized method pave the way for the low-cost and large-scale production of high-temperature thermal insulation. |
| Starting Page | 122 |
| e-ISSN | 23102861 |
| DOI | 10.3390/gels7030122 |
| Journal | Gels |
| Issue Number | 3 |
| Volume Number | 7 |
| Language | English |
| Publisher | MDPI |
| Publisher Date | 2021-08-14 |
| Access Restriction | Open |
| Subject Keyword | Gels Silica Aerogels Alumina-doped High Temperature Resistance Thermal Stability |
| Content Type | Text |
| Resource Type | Article |