The Effect of Thin Film Fabrication Techniques on the Performance of rGO Based $NO_{2}$ Gas Sensors at Room Temperature
Content Provider | MDPI |
---|---|
Author | Shahzad, Shazrah Wang, Huaipeng Li, Weiwei Sun, Yilin Xie, Dan Ren, Tian Ling |
Copyright Year | 2022 |
Description | Reduced graphene oxide (rGO) has attracted enormous interest as a promising candidate material for gas detection due to its large specific surface areas. In our work, rGO films were fabricated on a large scale using dip-coating and spin-coating methods for the detection of nitrogen dioxide $(NO_{2}$) gas at room temperature. The influence of different test environments on the sensing performance, including the test atmosphere, gas flow and gas pressure was evaluated. The response time of the dip-coating method was 573 s with a long recovery period of 639 s and for the spin-coating method, the response time and recovery time was 386 s and 577 s, respectively. In addition, the spin-coated sensor exhibited high selectivity to $NO_{2}$, with the response increasing by more than 20% (for 15 ppm $NO_{2}$) as compared with that for HCHO, $NH_{3}$, and $CH_{4}$. Our results indicated that the spin coating method was more suitable for rGO-based gas sensors with higher performance. |
Starting Page | 119 |
e-ISSN | 22279040 |
DOI | 10.3390/chemosensors10030119 |
Journal | Chemosensors |
Issue Number | 3 |
Volume Number | 10 |
Language | English |
Publisher | MDPI |
Publisher Date | 2022-03-21 |
Access Restriction | Open |
Subject Keyword | Chemosensors Reduced Graphene Oxide Fabrication Methods No2 Gas Sensor Room Temperature |
Content Type | Text |
Resource Type | Article |