NDLI: 40μm Ag/Au composite flip-chip interconnect using solid state atomic bonding at 200°C

Content Provider	IEEE Xplore Digital Library
Author	Lin, W.P. Chu-Hsuan Sha Lee, C.C.
Copyright Year	2012
Description	Author affiliation: Electrical Engineering and Computer Science, Materials and Manufacturing Technology, University of California, Irvine, Irvine, CA, USA, 92697-2660 (Lin, W.P.; Chu-Hsuan Sha; Lee, C.C.)
Abstract	We performed 40μm silver (Ag)/gold (Au) composite flip-chip interconnects joints between silicon (Si) chips and copper (Cu) substrate using solid-state bonding process at 200°C. 50×50 Ag/Au columns with 40μm in diameter and 100μm pitch were fabricated on a chip region by photolithographic and electroplating processes. Then, the Ag/Au columns were bonding to Cu substrate with fresh surface using solid-state at 200°C for five minutes with a static pressure of 1.7∼2.7 MPa (250∼400psi). The corresponding load for each column is 0.22∼0.35 gm. The five minutes is constrained by the equipment. In theory, bonding should occur in seconds. Cross section SEM images show that Ag/Au column is well bonded to Cu substrate with no void or breakage within it. Ag/Au composite joints well manage the shear strain induced by coefficient of thermal expansion (CTE) mismatch. There is no molten phase during the bonding process. Neither flux nor underfill was used. Compared to solder flip-chip joints, this new process has the reduction of electrical resistance of the joints of the same size by a factor of 6. Pull test was conducted. The fracture force and fracture strength are 6.5∼7.3kg and 2,940∼3,310psi (20.2∼22.8MPa), respectively. The fracture force is 2.5× of the criterion in MIL-STD-883E. The SEM/EDX analysis of the fracture interface showed that fracture of bonding interface is least likely to incur in pull test.
Starting Page	2070
Ending Page	2074
File Size	2236415
Page Count	5
File Format	PDF
ISBN	9781467319669
ISSN	05695503
e-ISBN	9781467319652
e-ISBN	9781467319645
DOI	10.1109/ECTC.2012.6249126
Language	English
Publisher	Institute of Electrical and Electronics Engineers, Inc. (IEEE)
Publisher Date	2012-05-29
Publisher Place	USA
Access Restriction	Subscribed
Rights Holder	Institute of Electrical and Electronics Engineers, Inc. (IEEE)
Subject Keyword	Gold Bonding Joints Silicon Substrates Flip chip gold flip-chip interconnect flip-chip joints electronic packaging bonding solid-state bonding silver
Content Type	Text
Resource Type	Article
Subject	Electronic, Optical and Magnetic Materials Electrical and Electronic Engineering

Sl.	Authority	Responsibilities	Communication Details
1	Ministry of Education (GoI), Department of Higher Education	Sanctioning Authority	https://www.education.gov.in/ict-initiatives
2	Indian Institute of Technology Kharagpur	Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project	https://www.iitkgp.ac.in
3	National Digital Library of India Office, Indian Institute of Technology Kharagpur	The administrative and infrastructural headquarters of the project	Dr. B. Sutradhar bsutra@ndl.gov.in
4	Project PI / Joint PI	Principal Investigator and Joint Principal Investigators of the project	Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon
5	Website/Portal (Helpdesk)	Queries regarding NDLI and its services	support@ndl.gov.in
6	Contents and Copyright Issues	Queries related to content curation and copyright issues	content@ndl.gov.in
7	National Digital Libarray of India Club (NDLI Club)	Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach	clubsupport@ndl.gov.in
8	Digital Preservation Centre (DPC)	Assistance with digitizing and archiving copyright-free printed books	dpc@ndl.gov.in
9	IDR Setup or Support	Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops	idr@ndl.gov.in

40μm Ag-AgIn flip-chip interconnect process at 180°C

10μm Ag flip-chip by solid-state bonding at 250°C

40-$mu{rm m}$ Cu/Au Flip-Chip Joints Made by 200$^{circ}{rm C}$ Solid-State Bonding Process

15μm Silver flip-chip technology with solid-state bonding

40 $mu{rm m}$ Flip-Chip Process Using Ag–In Transient Liquid Phase Reaction

40 μm Silver Flip-Chip Interconnect Technology With Solid-State Bonding

40 m Copper–Silver Composite Flip-Chip Interconnect Technology Using Solid-State Bonding

Low-Temperature Solid-State Silver Bonding of Silicon Chips to Alumina Substrates

Bonding Silicon Chips to Aluminum Substrates Using Ag–In System Without Flux

40μm Ag/Au composite flip-chip interconnect using solid state atomic bonding at 200°C

Similar Documents

40μm Ag-AgIn flip-chip interconnect process at 180°C

10μm Ag flip-chip by solid-state bonding at 250°C

40-$mu{rm m}$ Cu/Au Flip-Chip Joints Made by 200$^{circ}{rm C}$ Solid-State Bonding Process

15μm Silver flip-chip technology with solid-state bonding

40 $mu{rm m}$ Flip-Chip Process Using Ag–In Transient Liquid Phase Reaction

40 μm Silver Flip-Chip Interconnect Technology With Solid-State Bonding

40 m Copper–Silver Composite Flip-Chip Interconnect Technology Using Solid-State Bonding

Low-Temperature Solid-State Silver Bonding of Silicon Chips to Alumina Substrates

Bonding Silicon Chips to Aluminum Substrates Using Ag–In System Without Flux

40μm Ag/Au composite flip-chip interconnect using solid state atomic bonding at 200°C