Catalysts for ultrahigh current density oxygen cathodes for space fuel cell applications (Document No: 19920008147)
| Content Provider | NASA Technical Reports Server (NTRS) |
|---|---|
| Author | Tryk, Donald A. Yeager, E. |
| Copyright Year | 1992 |
| Description | The objective was to identify promising electrocatalyst/support systems for oxygen cathodes capable of operating at ultrahigh current densities in alkaline fuel cells. Such cells will require operation at relatively high temperatures and O2 pressures. A number of materials were prepared, including Pb-Ru and Pb-Ir pyrochlores, RuO2 and Pt-doped RuO2, lithiated NiO and La-Ni perovskites. Several of these materials were prepared using techniques that had not been previously used to prepare them. Particularly interesting was the use of the alkaline solution technique to prepare Pt-doped and Pb-Ru pyrochlores in high area form. Also interesting was the use of the fusion (melt) method for preparing the Pb-Ru pyrochlore. Several of the materials were also deposited with platinum. Well-crystallized Pb2Ru2O(7-y) was used to fabricate very high performance O2 cathodes with good stability in room temperature KOH. This material was also found to be stable over a useful potential range at approx. 140 C in concentrated KOH. For some of the samples, fabrication of the gas-fed electrodes could not be fully optimized during this project period. Future work may be directed at this problem. Pyrochlores that were not well-crystallized were found to be unstable in alkaline solution. Very good O2 reduction performance and stability were observed with Pb2RuO(7-y) in a carbon-based gas-fed electrode with an anion-conducting membrane placed on the electrolyte side of the electrode. The performance came within a factor of about two of that observed without carbon. High area platinum and gold supported on several conductive metal oxide supports were examined. Only small improvements in O2 reduction performance at room temperature were observed for Pb2Ru2O(7-y) as a support because of the high intrinsic activity of the pyrochlore. In contrast, a large improvement was observed for Li-doped NiO as a support for Pt. Very poor performance was observed for Au deposited on Li-NiO at approx. 150 C. Nearly reversible behavior was observed for the O2/OH(-) couple for Li-doped NiO at approx. 200 C. The temperature dependence for the O2 reduction was examined. |
| File Size | 5480776 |
| Page Count | 76 |
| File Format | |
| Alternate Webpage(s) | http://archive.org/details/NASA_NTRS_Archive_19920008147 |
| Archival Resource Key | ark:/13960/t7bs3q468 |
| Language | English |
| Publisher Date | 1992-01-13 |
| Access Restriction | Open |
| Subject Keyword | Spacecraft Propulsion And Power Gold Temperature Dependence Oxygen Catalysts Cell Cathodes Spacecraft Power Supplies Alkaline Batteries Potassium Hydroxides Perovskites Carbon Metal Oxides Platinum Fuel Cells Electrolytes Current Density Technology Utilization Ntrs Nasa Technical Reports Server (ntrs) Nasa Technical Reports Server Aerodynamics Aircraft Aerospace Engineering Aerospace Aeronautic Space Science |
| Content Type | Text |
| Resource Type | Technical Report |