Stress-corrosion behavior of aluminum-lithium alloys in aqueous environments

Content Provider	NASA Technical Reports Server (NTRS)
Author	Galvin, R. P. Nelson, H. G. Pizzo, P. P.
Copyright Year	1983
Description	The stress corrosion susceptibility of two powder metallurgy (P/M) alloys, Al-Li-Cu and Al-Li-Cu-Mg two mechanically attrited (M/A) alloys, Al-Li-Cu and Al-Li-Mg; and two wrought, ingot alloys, X-2020 and AA7475, are compared. Time-dependent fracture in an aqueous sodium chloride environment under alternate immersion condition was found to vary significantly between alloys. The stress corrosion behavior of the two powder metallurgy processed alloys was studied in detail under conditions of crack initiation, static crack growth, and fatigue crack growth. A variety of stress corrosion tests were performed including smooth surface, time-to-failure tests; potentiostatic tests on smooth surfaces exposed to constant applied strain rates; and fracture mechanics-type tests under static and cyclic loads. Both alloys show surface pitting and subsequent intergranular corrosion. Pitting is more severe in the magnesium-bearing alloy and is associated with stringer particles strung along the extrusion direction as a result of P/M processing.
File Size	1850363
Page Count	36
File Format	PDF
Alternate Webpage(s)	http://archive.org/details/NASA_NTRS_Archive_19840003188
Archival Resource Key	ark:/13960/t80k76q0d
Language	English
Publisher Date	1983-10-01
Access Restriction	Open
Subject Keyword	Metallic Materials Fracture Mechanics Cyclic Loads Aluminum Alloys Powder Metallurgy Lithium Alloys Sodium Chlorides Static Loads Intergranular Corrosion Pitting Stress Corrosion Aqueous Solutions Microstructure Crack Initiation Ntrs Nasa Technical Reports Server (ntrs) Nasa Technical Reports Server Aerodynamics Aircraft Aerospace Engineering Aerospace Aeronautic Space Science
Content Type	Text
Resource Type	Technical Report

Central Library (ISO-9001:2015 Certified)
Indian Institute of Technology Kharagpur
Kharagpur, West Bengal, India | PIN - 721302

See location in the Map
03222 282435
Mail: support@ndl.gov.in

Sl.	Authority	Responsibilities	Communication Details
1	Ministry of Education (GoI), Department of Higher Education	Sanctioning Authority	https://www.education.gov.in/ict-initiatives
2	Indian Institute of Technology Kharagpur	Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project	https://www.iitkgp.ac.in
3	National Digital Library of India Office, Indian Institute of Technology Kharagpur	The administrative and infrastructural headquarters of the project	Dr. B. Sutradhar bsutra@ndl.gov.in
4	Project PI / Joint PI	Principal Investigator and Joint Principal Investigators of the project	Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon
5	Website/Portal (Helpdesk)	Queries regarding NDLI and its services	support@ndl.gov.in
6	Contents and Copyright Issues	Queries related to content curation and copyright issues	content@ndl.gov.in
7	National Digital Library of India Club (NDLI Club)	Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach	clubsupport@ndl.gov.in
8	Digital Preservation Centre (DPC)	Assistance with digitizing and archiving copyright-free printed books	dpc@ndl.gov.in
9	IDR Setup or Support	Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops	idr@ndl.gov.in