Evaluation of commercially supplied silver coated teflon for spacecraft temperature control usage
| Content Provider | NASA Technical Reports Server (NTRS) |
|---|---|
| Author | Heaney, J. B. |
| Copyright Year | 1974 |
| Description | A series of tests are described which were performed to evaluate the acceptability of a commercially supplied silver backed teflon thermal control coating relative to teflon previously coated at GSFC. Optical measurements made on numerous samples indicate that the commercial material possesses an average solar absorptance of 0.085, an emittance of 0.76 and an average alpha/epsilon equal to 0.112, all of which are equivalent to the GSFC coated teflon. The emittance of the protective inconel backing was found to be 0.037. The coating is shown to have good adhesion at the Ag-teflon interface and exposure to UV irradiation uncovered no coating irregularities. Temperature cycling over the range -135 C to +200 C produced crazing in the evaporated Ag layer as expected but no delamination was observed. The suitability of Mystik no. 7366 and 3M no. 467 adhesives as bonding agents for the metallized polymer is demonstrated. Various problems associated with production reproducibility and selection of a proper bonding process are discussed. |
| File Size | 1343820 |
| Page Count | 34 |
| File Format | |
| Alternate Webpage(s) | http://archive.org/details/NASA_NTRS_Archive_19740009173 |
| Archival Resource Key | ark:/13960/t8md3q00j |
| Language | English |
| Publisher Date | 1974-01-01 |
| Access Restriction | Open |
| Subject Keyword | Materials, Nonmetallic Silver Performance Tests Thermal Control Coatings Irradiation Spacecraft Structures Spacecraft Temperature Bonding Inconel Trademark Teflon Trademark Ntrs Nasa Technical Reports Server (ntrs) Nasa Technical Reports Server Aerodynamics Aircraft Aerospace Engineering Aerospace Aeronautic Space Science |
| Content Type | Text |
| Resource Type | Article |