Exploratory study of friction welds in udimet 700 and td-nickel bar
| Content Provider | NASA Technical Reports Server (NTRS) |
|---|---|
| Author | Moore, T. J. |
| Copyright Year | 1971 |
| Description | Friction welded butt joints were made in both Udimet 700 and TD-Nickel bar. Also, dissimilar metal friction welds were made between these materials. Friction welding of Udimet 700 shows great promise because the welds were found to be as strong as the parent metal in stress rupture and tensile tests at 760 and 980 C. The weld line was not detectable metallographically in the heat treated condition. Friction welding for TD-Nickel, however, holds little if any promise. TD-Nickel friction weldments could support only 9 percent as much stress as the base metal for a 10-hour stress-rupture life at 1090 C. Dissimilar Udimet 700/TD-Nickel friction welds could sustain only 15 percent as much stress as the TD-Nickel parent metal for a 10-hour rupture life at 930 C. |
| File Size | 6519004 |
| Page Count | 21 |
| File Format | |
| Alternate Webpage(s) | http://archive.org/details/NASA_NTRS_Archive_19720003782 |
| Archival Resource Key | ark:/13960/t3pw17w2p |
| Language | English |
| Publisher Date | 1971-11-01 |
| Access Restriction | Open |
| Subject Keyword | Materials, Metallic Welded Joints Stress Analysis Nickel Alloys Weld Strength Weld Tests Mechanical Properties Friction Welding Butt Joints Ntrs Nasa Technical Reports Server (ntrs) Nasa Technical Reports Server Aerodynamics Aircraft Aerospace Engineering Aerospace Aeronautic Space Science |
| Content Type | Text |
| Resource Type | Technical Report |