| Author | Rotti, Rajeshwari B. Sunitha, D. V. Manjunath, Ramya Roy, Arpita Mayegowda, Shilpa Borehalli Gnanaprakash, A. P. Alghamdi, Saad Almehmadi, Mazen Abdulaziz, Osama Allahyani, Mamdouh Aljuaid, Abdulelah Alsaiari, Ahad Amer Ashgar, Sami S. Babalghith, Ahmad O. Abd El-Lateef, Amal Ezzat Khidir, Elshiekh B. |
| Abstract | Magnesium oxide (MgO) nanostructured particles (NP) were prepared using simple solution combustion technique using leaf extracts of Mangifera indica (Mango - Ma), Azadirachta indica (Neem - Ne) and Carica papaya (Papaya - Pa) as reducing agents. MgO nanostructures synthesized by leaf extracts were calcinated at 5000 C for two hours. To analyze the characteristics of obtained material – Ma-NP, Ne-NP and Pa-NP for dosimetry applications, thermoluminescence (TL) studies were carried out for Co-60 gamma rays irradiated samples in the dose range 10-50 KGy, PaNP and NeNP exhibited well defined glow curve, when compared with MaNP samples. In addition, it was observed that the TL intensity decreases and glow peak temperature shifted towards the higher temperature with the increase in heating rate. The glow peak was segregated using glow curve deconvolution and thermal cleaning method. Kinetic parameters estimated using Chen’s method, trap depth (E) and frequency factor (s) were found to be 0.699, 7.408, 0.4929 and 38.71, 11.008, 10.71for Pa-NP, Ne-NP, Ma-NP respectively. The well resolved glow curve, good linear behavior in the dose range 10 to 50 KGy and less fading was observed in PaNP then compared with MaNP and NeNP. Antibacterial activity was checked against human pathogens Escherichia coli, Staphylococcus aureus and Pseudomonas aeruginosa. A visible zone of clearance was observed at 200 and 100 µg/mL by the PaNP and NeNP, indicating the death of colonies by the nanoparticles. Therefore, PaNP nanomaterial is a potential phosphor material for dosimetry and antibacterial application compared to NeNP and MaNP. |
| ISSN | 22962646 |
| DOI | 10.3389/fchem.2023.1143614 |
| Volume Number | 11 |
| Journal | Frontiers in Chemistry |
| Language | English |
| Publisher Date | 2023-03-23 |
| Access Restriction | Open |
| Subject Keyword | Anti-bacterial activity Defects Thermoluminescence Dosimetry Green synthesis |
| Content Type | Text |
| Resource Type | Article |
| Subject | Chemistry |
National Digital Library of India (NDLI) is a virtual repository of learning resources which is not just a repository with search/browse facilities but provides a host of services for the learner community. It is sponsored and mentored by Ministry of Education, Government of India, through its National Mission on Education through Information and Communication Technology (NMEICT). Filtered and federated searching is employed to facilitate focused searching so that learners can find the right resource with least effort and in minimum time. NDLI provides user group-specific services such as Examination Preparatory for School and College students and job aspirants. Services for Researchers and general learners are also provided. NDLI is designed to hold content of any language and provides interface support for 10 most widely used Indian languages. It is built to provide support for all academic levels including researchers and life-long learners, all disciplines, all popular forms of access devices and differently-abled learners. It is designed to enable people to learn and prepare from best practices from all over the world and to facilitate researchers to perform inter-linked exploration from multiple sources. It is developed, operated and maintained from Indian Institute of Technology Kharagpur.
Learn more about this project from here.
NDLI is a conglomeration of freely available or institutionally contributed or donated or publisher managed contents. Almost all these contents are hosted and accessed from respective sources. The responsibility for authenticity, relevance, completeness, accuracy, reliability and suitability of these contents rests with the respective organization and NDLI has no responsibility or liability for these. Every effort is made to keep the NDLI portal up and running smoothly unless there are some unavoidable technical issues.
Ministry of Education, through its National Mission on Education through Information and Communication Technology (NMEICT), has sponsored and funded the National Digital Library of India (NDLI) project.
| Sl. | Authority | Responsibilities | Communication Details |
|---|---|---|---|
| 1 | Ministry of Education (GoI), Department of Higher Education |
Sanctioning Authority | https://www.education.gov.in/ict-initiatives |
| 2 | Indian Institute of Technology Kharagpur | Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project | https://www.iitkgp.ac.in |
| 3 | National Digital Library of India Office, Indian Institute of Technology Kharagpur | The administrative and infrastructural headquarters of the project | Dr. B. Sutradhar bsutra@ndl.gov.in |
| 4 | Project PI / Joint PI | Principal Investigator and Joint Principal Investigators of the project |
Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon |
| 5 | Website/Portal (Helpdesk) | Queries regarding NDLI and its services | support@ndl.gov.in |
| 6 | Contents and Copyright Issues | Queries related to content curation and copyright issues | content@ndl.gov.in |
| 7 | National Digital Library of India Club (NDLI Club) | Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach | clubsupport@ndl.gov.in |
| 8 | Digital Preservation Centre (DPC) | Assistance with digitizing and archiving copyright-free printed books | dpc@ndl.gov.in |
| 9 | IDR Setup or Support | Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops | idr@ndl.gov.in |
|
Loading...
|