| Content Provider | The American Society of Mechanical Engineers (ASME) Digital Collection |
|---|---|
| Author | Aune, Ragnhild Fostervoll, Hans Akselsen, Odd Magne |
| Copyright Year | 2003 |
| Abstract | Supermartensitic stainless steels are known to be prone to hydrogen induced cold cracking. Therefore, the objective of this work was to assess the susceptibility to hydrogen cracking in Gas Metal Arc Welding (GMAW) with use of matching base and filler materials (supermartensitic stainless steel), using the Instrumented Restraint Cracking (IRC) test. Root welding in the IRC test did not result in hydrogen induced cracking, neither for low nor high weld metal hydrogen content. Because of the martensitic transformation, the global residual stresses are very low after welding (below 100 MPa). Since the yield strength (Rp0.2%) of the material is about 600–720 MPa, it implies that the IRC test method is not very suitable for supermartensitic stainless steels. However, by performing IRC test multi-layer welding, micro-cracks were found in the last pass. An increase in the weld metal hydrogen content resulted in reduced fracture stress and ductility, as observed in tensile testing of IRC test specimens directly after welding. Investigation of the fracture surfaces of the specimens with high hydrogen contents showed fish eyes, which are strong indications of hydrogen embrittlement. By performing heat treatment (225°C for 24 hours) of specimens with high hydrogen contents and subsequent tensile testing, the fracture stress and ductility were restored to the initial base metal level. Slow Strain Rate Testing (SSRT) with and without Cathodic Protection (CP) was performed on test specimens sampled transverse to the welding direction. CP has detrimental effect on the fracture stress and ductility due to the high weld metal hydrogen pick up. |
| Sponsorship | Ocean, Offshore, and Arctic Engineering Division |
| Starting Page | 177 |
| Ending Page | 183 |
| Page Count | 7 |
| File Format | |
| ISBN | 0791836835 |
| DOI | 10.1115/OMAE2003-37282 |
| e-ISBN | 079183672X |
| Volume Number | Volume 3: Materials Technology; Ocean Engineering; Polar and Arctic Sciences and Technology; Workshops |
| Conference Proceedings | ASME 2003 22nd International Conference on Offshore Mechanics and Arctic Engineering |
| Language | English |
| Publisher Date | 2003-06-08 |
| Publisher Place | Cancun, Mexico |
| Access Restriction | Subscribed |
| Subject Keyword | Cathodic protection Supermartensitic stainless steels Hydrogen assisted cracking Cracking (materials) Fracture (process) Welding Hydrogen Stainless steel |
| Content Type | Text |
| Resource Type | Article |
National Digital Library of India (NDLI) is a virtual repository of learning resources which is not just a repository with search/browse facilities but provides a host of services for the learner community. It is sponsored and mentored by Ministry of Education, Government of India, through its National Mission on Education through Information and Communication Technology (NMEICT). Filtered and federated searching is employed to facilitate focused searching so that learners can find the right resource with least effort and in minimum time. NDLI provides user group-specific services such as Examination Preparatory for School and College students and job aspirants. Services for Researchers and general learners are also provided. NDLI is designed to hold content of any language and provides interface support for 10 most widely used Indian languages. It is built to provide support for all academic levels including researchers and life-long learners, all disciplines, all popular forms of access devices and differently-abled learners. It is designed to enable people to learn and prepare from best practices from all over the world and to facilitate researchers to perform inter-linked exploration from multiple sources. It is developed, operated and maintained from Indian Institute of Technology Kharagpur.
Learn more about this project from here.
NDLI is a conglomeration of freely available or institutionally contributed or donated or publisher managed contents. Almost all these contents are hosted and accessed from respective sources. The responsibility for authenticity, relevance, completeness, accuracy, reliability and suitability of these contents rests with the respective organization and NDLI has no responsibility or liability for these. Every effort is made to keep the NDLI portal up and running smoothly unless there are some unavoidable technical issues.
Ministry of Education, through its National Mission on Education through Information and Communication Technology (NMEICT), has sponsored and funded the National Digital Library of India (NDLI) project.
| Sl. | Authority | Responsibilities | Communication Details |
|---|---|---|---|
| 1 | Ministry of Education (GoI), Department of Higher Education |
Sanctioning Authority | https://www.education.gov.in/ict-initiatives |
| 2 | Indian Institute of Technology Kharagpur | Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project | https://www.iitkgp.ac.in |
| 3 | National Digital Library of India Office, Indian Institute of Technology Kharagpur | The administrative and infrastructural headquarters of the project | Dr. B. Sutradhar bsutra@ndl.gov.in |
| 4 | Project PI / Joint PI | Principal Investigator and Joint Principal Investigators of the project |
Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon |
| 5 | Website/Portal (Helpdesk) | Queries regarding NDLI and its services | support@ndl.gov.in |
| 6 | Contents and Copyright Issues | Queries related to content curation and copyright issues | content@ndl.gov.in |
| 7 | National Digital Library of India Club (NDLI Club) | Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach | clubsupport@ndl.gov.in |
| 8 | Digital Preservation Centre (DPC) | Assistance with digitizing and archiving copyright-free printed books | dpc@ndl.gov.in |
| 9 | IDR Setup or Support | Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops | idr@ndl.gov.in |
|
Loading...
|