NDLI: Fatigue and Crack Growth in 7050-T7451 Aluminum Alloy Under Constant- and Variable-Amplitude Loading

Content Provider	The American Society of Mechanical Engineers (ASME) Digital Collection
Author	James, C. Newman Justin, W. Shaw Balkrishna, S. Annigeri Brett, M. Ziegler
Copyright Year	2012
Abstract	The 7050 aluminum alloy is used in many aerospace structural applications. Previous studies have identified that fatigue cracks develop very rough crack-surface profiles, which cause very high crack-closure levels due to a combination of plasticity, roughness and debris. Previously, tests were conducted on compact, C(T), specimens to generate crack-growth data from threshold to near fracture over a wide range in stress ratios (R). New threshold testing methods, based on compression precracking, were used to generate the data in the near-threshold regime. The plasticity-induced crack-closure model, FASTRAN, was used to correlate the data over a wide range in stress ratios and crack-growth rates from threshold to near fracture. To account for the very high crack-closure levels, a very low constraint factor, like plane-stress conditions, had to be used in the model. In addition, the crack-opening loads were measured during these tests using a local strain-gage method to generate another ΔKeff-rate curve. These two curves differed only in the near-threshold regime. Herein, fatigue-crack-growth tests were conducted on C(T) specimens under spike overloads and simulated aircraft spectrum loading. Also, fatigue tests were conducted on single-edge-notch bend, SEN(B), specimens over a wide range in loading conditions (constant amplitude and three aircraft spectra). All specimens were machined from a single forged block of 7050-T7451. However, no residual stresses were measured in both the SEN(B) and C(T) specimens. Two European standard spectra were used, but modified to have only tension-tension loading. The purpose of this paper was to evaluate the two different effective stress-intensity factor curves for making crack-growth and fatigue-life predictions. Small-crack theory was used to make fatigue-life predictions using inclusion-particle sizes from the literature. Fatigue predictions on the SEN(B) specimens agreed fairly well (± 30%) using a 12-micrometer semi-circular initial flaw located at the semicircular-edge notch under all loading conditions, except the model was unconservative (factor of 3) on one of the severe aircraft spectra (Mini-TWIST+, Level 1). For the C(T) specimens subjected to single-spike overloads, the life-prediction code produced much more retardation than observed in the tests. However, the predicted crack-length-against-cycles under the Mini-Falstaff+ spectrum were only about 15% longer than the tests. The discrepancy under the single-spike overloads and the severe aircraft spectra was suspected to be caused by the low constraint factor and/or crack paths meandering around overload plastic zones. Ideally, a roughness-induced crack-closure model, in addition to the plasticity model, would be needed to obtain more reasonable results.
Sponsorship	International Gas Turbine Institute
Starting Page	131
Ending Page	141
Page Count	11
File Format	PDF
ISBN	9780791844731
DOI	10.1115/GT2012-68502
Volume Number	Volume 7: Structures and Dynamics, Parts A and B
Conference Proceedings	ASME Turbo Expo 2012: Turbine Technical Conference and Exposition
Language	English
Publisher Date	2012-06-11
Publisher Place	Copenhagen, Denmark
Access Restriction	Subscribed
Subject Keyword	Cracks Plasticity Roughness Fatigue Spectrum loading Fatigue-crack growth Debris Crack closure Aluminum alloy Aluminum alloys Surface roughness Fracture (materials) Fatigue cracks
Content Type	Text
Resource Type	Article

Sl.	Authority	Responsibilities	Communication Details
1	Ministry of Education (GoI), Department of Higher Education	Sanctioning Authority	https://www.education.gov.in/ict-initiatives
2	Indian Institute of Technology Kharagpur	Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project	https://www.iitkgp.ac.in
3	National Digital Library of India Office, Indian Institute of Technology Kharagpur	The administrative and infrastructural headquarters of the project	Dr. B. Sutradhar bsutra@ndl.gov.in
4	Project PI / Joint PI	Principal Investigator and Joint Principal Investigators of the project	Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon
5	Website/Portal (Helpdesk)	Queries regarding NDLI and its services	support@ndl.gov.in
6	Contents and Copyright Issues	Queries related to content curation and copyright issues	content@ndl.gov.in
7	National Digital Library of India Club (NDLI Club)	Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach	clubsupport@ndl.gov.in
8	Digital Preservation Centre (DPC)	Assistance with digitizing and archiving copyright-free printed books	dpc@ndl.gov.in
9	IDR Setup or Support	Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops	idr@ndl.gov.in