NDLI: Critical Plane Fatigue Modeling and Characterization of Single Crystal Nickel Superalloys

Content Provider	The American Society of Mechanical Engineers (ASME) Digital Collection
Author	Rajiv, A. Naik Daniel, P. Deluca Dilip, M. Shah
Copyright Year	2002
Abstract	Single crystal nickel-base superalloys deform by shearing along <111> planes, sometimes referred to as “octahedral” slip planes. Under fatigue loading, cyclic stress produces alternating slip reversals on the critical slip systems which eventually results in fatigue crack initiation along the ‘critical’ octahedral planes. A ‘critical plane’ fatigue modeling approach was developed in the present study to analyze high cycle fatigue (HCF) failures in single crystal materials. This approach accounted for the effects of crystal orientation and the micromechanics of the deformation and slip mechanisms observed in single crystal materials. Three-dimensional (3-D) stress and strain transformation equations were developed to determine stresses and strains along the crystallographic octahedral planes and corresponding slip systems. These stresses and strains were then used to calculate several multiaxial critical plane parameters to determine the amount of fatigue damage and also the ‘critical planes’ along which HCF failures would initiate. The computed fatigue damage parameters were used along with experimentally measured fatigue lives, at 1100° F, to correlate the data for different loading orientations. Microscopic observations of the fracture surfaces were used to determine the actual octahedral plane (or facet) on which fatigue initiation occurred. X-ray diffraction measurements were then used to uniquely identify this damage initiation facet with respect to the crystal orientation in each specimen. These experimentally determined HCF initiation planes were compared with the analytically predicted ‘critical planes’.
Sponsorship	International Gas Turbine Institute
Starting Page	675
Ending Page	682
Page Count	8
File Format	PDF
ISBN	0791836096
DOI	10.1115/GT2002-30300
e-ISBN	0791836010
Volume Number	Volume 4: Turbo Expo 2002, Parts A and B
Conference Proceedings	ASME Turbo Expo 2002: Power for Land, Sea, and Air
Language	English
Publisher Date	2002-06-03
Publisher Place	Amsterdam, The Netherlands
Access Restriction	Subscribed
Subject Keyword	Deformation High cycle fatigue Shearing (deformation) Crystals X-ray diffraction Fatigue Fracture (materials) Superalloys Modeling Stress Fracture (process) Nickel Damage Die cutting Failure Fatigue damage Fatigue cracks Micromechanics (engineering) Crystal structure
Content Type	Text
Resource Type	Article

Sl.	Authority	Responsibilities	Communication Details
1	Ministry of Education (GoI), Department of Higher Education	Sanctioning Authority	https://www.education.gov.in/ict-initiatives
2	Indian Institute of Technology Kharagpur	Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project	https://www.iitkgp.ac.in
3	National Digital Library of India Office, Indian Institute of Technology Kharagpur	The administrative and infrastructural headquarters of the project	Dr. B. Sutradhar bsutra@ndl.gov.in
4	Project PI / Joint PI	Principal Investigator and Joint Principal Investigators of the project	Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon
5	Website/Portal (Helpdesk)	Queries regarding NDLI and its services	support@ndl.gov.in
6	Contents and Copyright Issues	Queries related to content curation and copyright issues	content@ndl.gov.in
7	National Digital Library of India Club (NDLI Club)	Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach	clubsupport@ndl.gov.in
8	Digital Preservation Centre (DPC)	Assistance with digitizing and archiving copyright-free printed books	dpc@ndl.gov.in
9	IDR Setup or Support	Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops	idr@ndl.gov.in