NDLI: Bond strength of resin composite to light activated bleached enamel

Content Provider	African Journals Online (AJOL)
Author	O.Y. Ozyilmaz T Yavuz F Aykent A.N. Ozturk
Abstract	Objectives: This study evaluated the microtensile bond strength (μTBS) of a resin composite bonded to bleached enamel as a function of bleaching conditions.Materials and Methods: The whiteness hydrogen peroxide (HP) bleaching agent containing 35% HP was applied to the central incisors’ facial enamel surface and irradiated as follows: No treatment (G1; control); no light (G2); light‑emitting diode, the 40s (G3); diode laser, the 20s (G4); and neodymium:yttrium aluminum garnet laser, 20s (G5). A Variolink II resin composite structure was then built up incrementally on the surface. The teeth were sectioned into three 1.2 mm × 1.2 mm wide “I”‑shaped sections. The specimens were then subjected to microtensile testing at a crosshead speed of 1 mm/min. Data were analyzed using one‑way ANOVA (α =0.05) followed by the Tukey Honestly Significant Difference post‑hoc test. The fractured surfaces were observed with a stereomicroscope at × 100 magnification.Results: One‑way ANOVA revealed no statistical differences among the groups (P > 0.05). No differences appeared between the groups bonded 14 days after bleaching (P > 0.05). Mean μTBS values (MPa) were as follows: 22.05 ± 5.01 (G1); 19.6 ± 5.6 (G2); 19.3 ± 5.4 (G3); 20.08 ± 2.08 (G4); and 18.1 ± 4.8 (G5). Many adhesive failures occurred at the bleached and irradiated enamel surfaces.Conclusion: The various irradiation treatments following the application of the whiteness HP bleaching agent to enamel did not significantly reduce the μTBS within a 14‑day period.
Ending Page	771
Starting Page	766
File Format	PDF
ISSN	11193077
e-ISSN	22297731
DOI	10.4103/1119-3077.178909
Journal	Nigerian Journal of Clinical Practice
Issue Number	6
Volume Number	19
Language	English
Publisher Date	2016-11-07
Access Restriction	Open
Subject Keyword	Health Bleaching agents lasers lasers neodymium yttrium aluminum garnet resin bonding tooth bleaching
Content Type	Text
Resource Type	Article
Subject	Medicine

Sl.	Authority	Responsibilities	Communication Details
1	Ministry of Education (GoI), Department of Higher Education	Sanctioning Authority	https://www.education.gov.in/ict-initiatives
2	Indian Institute of Technology Kharagpur	Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project	https://www.iitkgp.ac.in
3	National Digital Library of India Office, Indian Institute of Technology Kharagpur	The administrative and infrastructural headquarters of the project	Dr. B. Sutradhar bsutra@ndl.gov.in
4	Project PI / Joint PI	Principal Investigator and Joint Principal Investigators of the project	Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon
5	Website/Portal (Helpdesk)	Queries regarding NDLI and its services	support@ndl.gov.in
6	Contents and Copyright Issues	Queries related to content curation and copyright issues	content@ndl.gov.in
7	National Digital Library of India Club (NDLI Club)	Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach	clubsupport@ndl.gov.in
8	Digital Preservation Centre (DPC)	Assistance with digitizing and archiving copyright-free printed books	dpc@ndl.gov.in
9	IDR Setup or Support	Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops	idr@ndl.gov.in